Research Article | Open Access
Dong-Li Meng, Chun-Hui Chen, Jun-Dong Yi, Qiao Wu, Jun Liang, Yuan-Biao Huang, Rong Cao, "Migration-Prevention Strategy to Fabricate Single-Atom Fe Implanted N-Doped Porous Carbons for Efficient Oxygen Reduction", Research, vol. 2019, Article ID 1768595, 12 pages, 2019. https://doi.org/10.34133/2019/1768595
Migration-Prevention Strategy to Fabricate Single-Atom Fe Implanted N-Doped Porous Carbons for Efficient Oxygen Reduction
It is highly desired but challenging to achieve highly active single-atom Fe sites from iron-based metal-organic frameworks (MOFs) for efficient oxygen reduction reaction (ORR) due to the easy aggregation of iron species and formation of the inactive Fe-based particles during pyrolysis. Herein, a facile migration-prevention strategy is developed involving the incorporation of polyaniline (PANI) into the pores of iron porphyrinic-based MOF PCN-224(Fe) and followed by pyrolysis to obtain the single-atom Fe implanted N-doped porous carbons material PANI@PCN-224(Fe)-900. The introduced PANI inside the pores of PCN-224(Fe) not only served as protective fences to prevent the aggregation of the iron species during thermal annealing, but also acted as nitrogen sources to increase the nitrogen content and form Fe--C active sites. Compared with the pristine PCN-224(Fe) derived carbonization sample containing Fe-based particles, the carbonaceous material PANI@PCN-224(Fe)-900 without inactive Fe-based particles exhibited superb ORR electrocatalytic activity with a more positive half-wave potential, significantly improved stability in both alkaline media, and more challenging acidic condition. The migration-prevention strategy provides a new way to fabricate atomically dispersed metal active sites via pyrolysis approach for promoting catalysis.
The increase of environmental pollution and global energy demands promotes the development of the environmentally friendly energy conversion devices to avoid the use of fossil fuels [1–6]; among these, polymer electrolyte membrane fuel cell (PEMFC) and metal-air batteries can be as promising candidates in transportation vehicles and other power applications. However, the sluggish cathodic oxygen reduction reaction (ORR) has greatly hampered their development in commercial applications [7–9]. Although the platinum-based electrodes have been proved to be the most effective catalysts for ORR in both alkaline and acidic electrolytes [10–12], the high cost, scarcity, poor durability; and methanol-crossover hinder its commercialization process . Thus, tremendous efforts have been devoted to develop nonprecious metal catalysts to replace the Pt-based electrodes [13–24]. Among of them, single-atom Fe anchored on N-doped porous carbons to form Fe--C material is regarded as highly efficient active sites for ORR [16, 25–36]. Generally, the Fe--C electrocatalysts are obtained by pyrolysis of precursors containing iron and nitrogen species [31, 37, 38]. However, the aggregation of iron species usually occurs during the pyrolysis process, which leads to the formation of large amounts of inactive aggregates, such as iron and Fe-C nanoparticles .
In recent years, metal-organic frameworks (MOFs) constructed by coordinate bonds between organic linkers and metal ions have attracted extensive attention in gas adsorption and catalysis because of their large surface areas, tunable structures, and pore sizes [39–42]. Particularly, heteroatoms are uniformed distributed in the highly ordered frameworks make MOFs as self-sacrificed precursors/templates for the fabrication of the highly efficient single-atom metal implanted carbon-based electrocatalysts [43, 44]. The unique structures of MOFs could endow the obtained electrocatalysts with large specific surface areas and the uniform distribution of heteroatom dopants [45–49]. However, the adjacent metal ions with no protective layer between the pores of MOF are usually prone to aggregate to form inactive metal-based nanoparticles during thermal pyrolysis. Therefore, it is imperative to develop a general approach to prevent the aggregation of metal species and fabricate active metal sites at atomic level for highly efficient ORR.
With the above in mind, a migration-prevention strategy was proposed to fabricate single-metal-atom catalyst via inhibition the aggregation of the metal species to form inactive metal-based particles (Figure 1). As a proof of concept, polyaniline (PANI) was in situ inserted in the pores of iron porphyrinic-based MOF PCN-224(Fe), [(Zr6O4(OH)10(H2O)6)(Fe-TCPP)1.5 (Fe-TCPP = 5,10,15,20-Tetrakis(4-carboxyphenyl)porphyrinato]-Fe(III) Chloride) . During pyrolysis process, the PANI in the pores of PCN-224(Fe) as protective fence can prevent the aggregation of the adjacent iron species between the pores. Interestingly, PANI containing nitrogen-rich element could not only promote the formation of the N-doped carbon sites, but also capture the iron species and stabilize the atomically dispersed Fe- active sites. Thus, owning to the “partition role” of PANI, the obtained carbonaceous material PANI@PCN-224(Fe)-900 has abundant single-atom Fe active sites, large surface area, high conductivity, and nitrogen content. It exhibited highly efficient ORR activity and ultrahigh stability, far surpassing the pristine PCN-224(Fe) derived carbon materials PCN-224(Fe)-900 in both alkaline and acidic media. Moreover, the extremely good ORR performance of PANI@PCN-224(Fe)-900 with a half-wave potential (E1/2 = 0.893 V) also outdistanced the commercial Pt/C catalysts (E1/2 = 0.856 V) under alkaline conditions. More importantly, it exhibited comparable half-wave potential (E1/2 = 0.756 V) to that of the state-of-the-art Pt/C (0.783 V) in more challenging acidic media.
2. Results and Discussion
As we know, PANI is usually synthesized by oxidizing aniline using ammonium peroxodisulfate as catalyst . However, it is difficult to completely remove the catalysts residual from the system, which could in turn bring negative impact on the sensitive electrocatalytic system . Therefore, PCN-224(Fe) was selected as host to encapsulate PANI, in which the iron(III) porphyrin moieties in the pore wall (Figures S1 and S2) can catalyze the oxidative polymerization of aniline to form PANI with the aid of the environmentally friendly cocatalyst H2O2 . The self-catalysis strategy is no need to use of any other catalyst that is difficult for removal in the MOF, thus avoiding the introduction of residues to affect the electrocatalysis. The iron ions were coordinated by the porphyrin units in PCN-224 by using postsynthesis method (PSM). The powder X-ray diffraction (PXRD) patterns of PCN-224(Fe) were not changed in comparision with those of PCN-224 (Figure 2(a)). After PSM treatment, the obtained PCN-224(Fe) still has high Brunauer–Emmett–Teller (BET) surface area of 898 m2g−1 (Figure S2(a)) and large hydrophilic pore (1.8 nm) (Figure S2(b)), which facilitates the adsorption of aniline. To investigate the migration-prevention effect, the different loading amounts of PANI in the pores of PCN-224(Fe) were controlled by the adsorption time and as high as 27 wt% PANI can be inserted into its channels after 12 h adsorption. The obtained composites are designated as X-PANI@PCN-224(Fe) (X = 15% and 27%), where X is the mass fraction of PANI. Notably, PANI@PCN-224(Fe) was referred to as 27%-PANI@PCN-224(Fe) in this article. For comparison, PANI was isolated from PANI@PCN-224(Fe) by digestion of PCN-224(Fe) with strong alkali solution.
After polymerization, the brown PCN-224(Fe) was become to olive-green (Figure 2(b)), indicating that PANI had been inserted in the pores of PCN-224(Fe). The successful insertion of PANI into PCN-224(Fe) was further proved by FT-IR spectra and UV-Vis diffuse reflectance spectra. As shown from the FT-IR spectra in Figure S3, the bands at 1586 and 1489 cm−1 are attributed to quinone and benzine ring deformation of PANI, respectively , while the bands at 1300 and 1240 cm−1 are due to C-N and C=N stretching of the secondary aromatic amine. The peaks of quinonoid and benzenoid units of PANI in PANI@PCN-224(Fe) were observed at 1150 cm−1 and 820 cm−1, respectively. The UV-Vis spectra of the isolated PANI, PANI@PCN-224(Fe), and PCN-224(Fe) are displayed in Figure S4. The peaks at 322 and 931 nm in PANI@PCN-224(Fe) were contributed by and polaron band transitions of PANI . Moreover, the peaks at 424, 501, and 618 nm are corresponding to Soret band and Q band of iron porphyrin motifs in PANI@PCN-224(Fe), suggesting that the iron porphyrin based framework was stable during the self-catalysis synthesis of PANI. The PXRD patterns of PANI@PCN-224(Fe) (Figure 2) are coincident with those of PCN-224(Fe), further indicating that the structure of PCN-224(Fe) was still maintained during the polymerization process. Moreover, the sharp decrease of BET surface area (271 m2g−1) and pore size (with a diameter of ~ 0.66 and 1 nm) of PANI@PCN-224(Fe) after the loading of PANI (Figures S2(a) and S2(b)) suggested that most of pores have been filled by PANI. The TEM images show that the cubic PANI@PCN-224(Fe) appeared a much darker contrast than PCN-224(Fe) (Figures 2(c) and 2(d)), further indicating that the pores have been occupied by PANI.
After thermo-treatment at 900°C, no identifiable peak of Fe-based particles was observed in the PXRD (Figure S5) of PANI@PCN-224(Fe)-900 before acid etching. By contrast, the peaks of Fe and Fe3C particles were detected in PCN-224(Fe) derived materials PCN-224(Fe)-900. The results suggested that the inserted PANI in PANI@PCN-224(Fe)-900 indeed plays a protective fence role in preventing the aggregation of Fe elements during the pyrolyzing process. After removal of ZrO2 by HF etching, two apparent broad peaks centered at about 26° and 43° are observed in both of the PXRD patterns of PCN-224(Fe)-900 and PANI@PCN-224(Fe)-900, indicating that high degree of graphitic carbon with (002) and (100)/(101) diffractions was obtained (Figure 3(a)). The Raman spectra show (Figure 3(b)) two characteristic carbon resonances assigned to the G-band (1600 cm−1) and D-band (1350 cm−1), which correspond to graphitic sp2-hybridized carbon and sp3 carbon, respectively . The relatively higher intensity ratio () of PANI@PCN-224(Fe)-900 was compared with PCN-224(Fe)-900, suggesting abundant carbon defective active sites were generated due to the introduction of N-riched PANI. Electrochemical impedance (EIS) measurement showed that the minimum semicircle of the Nyquist plots for PANI@PCN-224(Fe)-900 is observed, suggesting the best conductivity among the carbonaceous materials (Figure S6). This is because the fact that the inserted PANI backbone throughout PCN-224(Fe) channels could prevent the pores collapse and the PANI-derived carbon can behave as interconnection for electrons transportation between internal surfaces . Thus, as shown in Figure 3(c), PANI@PCN-224(Fe)-900 shows larger N2 adsorption uptake and 1.7 times higher BET surface area (430 m2g−1) in comparison with PCN-224(Fe)-900 (252 m2g−1). In addition, both PCN-224(Fe)-900 and PANI@PCN-224(Fe)-900 have obvious desorption hysteresis loops, indicating mesopores were produced (Figure S7), which were favorable for the diffusion of the electrolyte and accessible to the active sites.
As shown in Figure 4(a), the TEM images reveal that, after pyrolysis, the cubic PCN-224(Fe) (Figure 2(c) and Figure S8(a)) becomes elliptical PCN-224(Fe)-900 with inconsecutive mesoporous structures, indicating the skeleton collapse happened upon pyrolysis. In contrast, PANI@PCN-224(Fe)-900 exhibits denser structure containing smaller pores due to the inserted PANI-derivated carbons (Figure 4(c)). Furthermore, Fe3C/Fe nanoparticles (NPs) with a lattice distance of 0.20 nm can be observed in the high-resolution TEM image (HRTEM, Figure 4(b)) of PCN-224(Fe)-900, while no visible Fe-based NP was detected in PANI@PCN-224(Fe)-900 (Figure 4(c), Figure S9). The aberration-corrected HAADF-STEM revealed single Fe atoms distributed in carbonaceous matrix, as the atomic dispersed bright spots were detected (Figure 4(d)). Further inspection by elemental mapping (Figure 4(e)), Fe and N elements are homogenously distributed throughout the whole carbonaceous matrix of PANI@PCN-224(Fe)-900. The results were in consistent with the PXRD (Figure S5 and Figure 3(a)) and Raman spectra (Figure 3(b)). This is because the fact that the inserted PANI could form nonporous carbon with densely stacked 2D layer structure (Figure S8(b)), which could behave as a promising protective fence to prevent the migration of the iron species to form Fe NPs during thermal annealing. The HRTEM image shows (Figure S9) abundant graphitic carbon crystalline structure is presented in PANI@PCN-224(Fe)-900, as the distinct lattice fringes with an interplanar space of 0.34 nm corresponding to the (002) plane of graphite can be observed. Such highly graphitic structure could facilitate the electron transport and thus will improve electrocatalytic activity.
X-ray photoelectron spectroscopy (XPS) measurements also demonstrated that both of PCN-224(Fe)-900 and PANI@PCN-224(Fe)-900 samples contain Fe, N, and C elements (Figure S10). The high-resolution N 1s spectra can be deconvoluted into pyridinic N (398.2 eV), Fe-Nx (399.4 ± 0.2 eV), pyrrolic N (400.5 ± 0.1 eV), graphitic N (401.4 ± 0.2 eV), and oxidized N (403.2 ± 0.2 eV) (Figure 5(a) and Figures S11(a) and S11(b)) . Notably, the relative ratio of Fe-Nx with other nitrogen species in PANI@PCN-224(Fe)-900 is much higher than that of PCN-224(Fe)-900 (Figure 5(b)). For iron species, two peaks at 710 and 721.9 eV in the high-resolution Fe 2p spectrum of PANI@PCN-224(Fe)-900 suggested that Fe2+ species was dominated in this sample, which may be coordinated with nitrogen that inherited from Fe-TCPP (Figure S11(c)) [27, 28, 58]. Furthermore, according to the elemental analysis (EA, Table S1) and inductively coupled plasma atomic emission spectroscopy (ICP-AES, Table S2) results, both of the N and Fe element contents in X-PANI@PCN-224(Fe)-900 increase along with the increasing of the inserted PANI content. It is also worth mentioning that PANI@PCN-224(Fe)-900 has much higher amounts of N and Fe element than those of PCN-224(Fe)-900 (Tables S1 and S2 and Figure S11). The results benefit from the fact that the PANI in PANI@PCN-224(Fe)-900 could provide effective protective layers and prevent the Fe species migrating and aggregating to form particles during pyrolysis. Moreover, the escaped iron element from Fe-TCPP units during annealing could be captured by the inserted PANI-derived N-doped carbon to stabilize atomic Fe- species [25, 38, 59–61]. Thus, PANI@PCN-224(Fe)-900 has a higher Fe amount of 1.89 wt%, while only 0.27 wt% Fe content comprising part of Fe3C/Fe was detected in PCN-224(Fe)-900 (Figure S5 and Figure 4(b)). The very low Fe amount in PCN-224(Fe)-900 is due to the Fe ions which were lack of protection and easy formed aggregated Fe-based NPs, which were leached by acid etching. In addition, the inserted PANI could also act as nitrogen sources to increase the nitrogen content and nitrogen-containing carbon active-site density of PANI@PCN-224(Fe)-900 (Figures S11(d) and S12), which could enhance synergistically for ORR in combination with Fe- sites [38, 62, 63]. To further identify the electronic and structural status of iron species in PANI@PCN-224(Fe)-900 and PCN-224(Fe)-900, X-ray absorption near-edge structure (XANES) and X-ray absorption fine structure (EXAFS) were performed (Figures 5(c) and 5(d)). The absorption edge energy of Fe K-edge in PANI@PCN-224(Fe)-900 and PCN-224(Fe)-900 located between Fe foil and 5,10,15,20-tetrakis(4-cyanophenyl)porphyrinato]-Fe(III) chloride (Fe-TPPCN), implying the positively charged iron species in both of the two samples, which are consistent with the XPS results. Furthermore, a weak pre-edge peak at 7112 eV was observed in both of PANI@PCN-224(Fe)-900 and PCN-224(Fe)-900, which is recognized as a fingerprint of symmetry and suggested the existence of Fe-N4 square-planar structure [25, 33, 64]. The analysis of Fe K-edge of EXAFS further revealed that atomic Fe- species was predominated in PANI@PCN-224(Fe)-900, while PCN-224(Fe)-900 contains the N-coordinated Fe and a large amount of Fe-based NPs including Fe3C and Fe. As shown in Figure 5(d), the main signal at 1.47 Å that assigned to the Fe-N scattering path further revealed that the Fe species in PANI@PCN-224(Fe)-900 was predominant Fe- configuration [32, 65]. Notably, compared with the R value (1.47 Å) in PANI@PCN-224(Fe)-900, the corresponding value of Fe(Cl)-N4 peak in Fe-TPPCN molecule shifts to 1.59 Å, which is ascribed to that the axial chlorine atom perpendicular to the Fe-N4 plane elongates the Fe-N bond distance [25, 26, 31, 66–68]. Nevertheless, the partial R values overlap between PANI@PCN-224(Fe)-900 and Fe-TPPCN suggests the existence of Fe-N4 and Fe-N5 species, which is difficult to use suitable coordination model to fit. The emergence of Fe-N5, in which one axial nitrogen atom is perpendicular to the Fe-N4 plane, was attributed to the nitrogen of the inserted PANI-derived carbon. More importantly, no obvious signals ascribed to Fe-Fe (2.2 Å) can be detected, manifesting the atomic dispersion of iron in PANI@PCN-224(Fe)-900. By contrast, the EXAFS curves of PCN-224(Fe)-900 exhibited a strong peak at 1.94 Å, which is more like the Fe-Fe distance in Fe3C and metallic Fe [27, 30]. These results confirmed that Fe-based NPs were presented in PCN-224(Fe)-900, which is consistent with the high-resolution TEM observation (Figure 4(b)). Taken together, the highly porous PANI@PCN-224(Fe)-900 with graphitic structure contains abundant single-atom Fe- sites, which is believed to show highly active in electrocatalysis for ORR.
To assess the electrocatalytic performance of PANI@PCN-224(Fe)-900, ORR was firstly investigated on a rotating disk electrode (RDE) in O2-saturated 0.1 M KOH. As shown in Figure 6(a), the linear sweep voltammetry (LSV) curves reveal that PANI@PCN-224(Fe)-900 has a more positive half-wave potential (E1/2 = 0.893 V vs. RHE, all the potentials are referenced with RHE), 70 mV higher than PCN-224(Fe)-900 (E1/2 = 0.823 V), even 37 mV higher than the commercial 20 wt% Pt/C (E1/2 = 0.856 V, Alfa Aesar), indicating that the single Fe atoms contribute much to the ORR performance of PANI@PCN-224(Fe)-900. The influence of PANI content on ORR activity was also studied (Figure 6(a)). 15%-PANI@PCN-224(Fe)-900 displays comparable ORR performance (E1/2 = 0.870 V) with Pt/C, much better than PCN-224(Fe)-900, although it was less well-behaved in comparison with PANI@PCN-224(Fe)-900. It is due to the introduction of PANI, which acted as protective fence to increase to amount of Fe single-atom. A sufficient quantity of Fe single-atom active sites was generated; it is enough for PANI@PCN-224(Fe)-900 to surpass the state-of-the-art Pt/C. Thus, among the four samples, PANI@PCN-224(Fe)-900 displays the most positive onset potential (1.01 V), which far outdistanced those of 15%-PANI@PCN-224(Fe)-900 (0.977 V), PCN-224(Fe)-900 (0.94 V), Pt/C (0.973 V), and PANI-900 (0.75 V). Moreover, PANI@PCN-224(Fe)-900 shows the largest diffusion-limiting current density of 7.17 mA cm−2 at 0.2 V vs. RHE with 1600 rpm among the related catalysts, confirming its superb electrocatalytic activity. The excellent ORR activity of PANI@PCN-224(Fe)-900 was also verified by the smallest Tafel slope (62 mV dec−1, Figure 6(b)), in comparison with those of PCN-224(Fe)-900 (73 mV dec−1), Pt/C (77 mV dec−1), and PANI-900 (92 mV dec−1). The electron transfer number (n) of PANI@PCN-224(Fe)-900 calculated according to rotating ring-disk electrode (RRDE) is 3.95 (E = 0.2 V), which is similar to that of Pt/C (n = 3.95), suggesting an efficient four-electron ORR pathway (Figure 6(c)). The methanol-crossover effects and durability of PANI@PCN-224(Fe)-900 were also examined. After 8 h of continuous polarization (Figure 6(d)), only 7% current density loss was observed in PANI@PCN-224(Fe)-900, while 27% current decrease was observed for Pt/C, which exemplified the good durability of PANI@PCN-224(Fe)-900. Additionally, PANI@PCN-224(Fe)-900 also demonstrated a superior tolerance against crossover effect of methanol under alkaline condition, which was much better than the Pt/C (Figure 6(e) and Figure S13). It is worth noting that PANI@PCN-224(Fe)-900 possesses one of the best ORR performance among all the reported nonnoble metal catalysts under alkaline condition (Table S3). Encouraged by the excellent ORR performance of PANI@PCN-224(Fe)-900 in alkaline media, we further explored its ORR activity in the more challenging acidic condition (0.1 M HClO4). Surprisingly, a more positive E1/2 of 0.756 V for PANI@PCN-224(Fe)-900 was achieved (Figure 6(f)), which is much more than PANI-900 (no active), 15%-PANI@PCN-224(Fe)-900 (0.74 V), and PCN-224(Fe)-900 (0.707 V), even comparable to that of benchmark Pt/C (0.783 V). Furthermore, PANI@PCN-224(Fe)-900 has the largest diffusion-limiting current density (7.78 mA cm−2, Figure 6(d)) at 0.1 V vs. RHE, which is higher than those of PCN-224(Fe)-900 (6.14 mA cm−2) and Pt/C (6.84 mA cm−2). Moreover, the small Tafel slope (82 mV dec−1, Figure 6(g)) of PANI@PCN-224(Fe)-900 is comparable to that of Pt/C (81 mV dec−1) and an ideal 4e- transfer process (n = 3.93, Figure S14) based on RRDE further manifests the superior ORR activity of PANI@PCN-224(Fe)-900. Moreover, PANI@PCN-224(Fe)-900 exhibited long-term durability, in contrast with Pt/C, which showed poor stability in acid media (Figure 6(h)). The much better tolerance to methanol performance for PANI@PCN-224(Fe)-900 in comparison with Pt/C was also demonstrated the advantage of the single-atom Fe- sites (Figure S15). Notably, the ORR activity of PANI@PCN-224(Fe)-900 in acidic media is also one of the best reported nonprecious metal catalysts (Table S4).
The above results suggested that the atomically dispersed Fe- is believed to be the highly active sites in PANI@PCN-224(Fe)-900 for ORR. The Fe-free catalyst PCN-224-900 showed very poor activity for the ORR, especially in acidic media (Figure S16), indicating that the activity of PANI@PCN-224(Fe)-900 catalyst mainly stems from Fe site. The SCN- poisoning experiment was further carried out to confirm the active site, as SCN- displays strong affinity to Fe ion. As shown in Figure 6(i), the diffusion-limiting current density of PANI@PCN-224(Fe)-900 for ORR in 0.1 M KOH decreased obviously from 7.17 mA cm−2 to 6.47 mA cm−2 (0.2 V vs. RHE), while the half-wave potential decreased significantly by 50 mV. Thus, the poisoning experiment clearly revealed that Fe- was verified to be the active site in PANI@PCN-224(Fe)-900 for ORR.
In summary, we have developed a facile migration-prevention strategy to fabricate Fe single-atom anchored on N-doped porous carbons to boost oxygen reduction reaction. The nitrogen-riched polymer PANI was in situ synthesized and inserted in the channels of PCN-224(Fe) catalyzed by the Fe-TCPP active sites in the pore walls. The inserted PANI-derived N-doped carbon was acted as protective fences to prohibit the aggregation of iron species to form inactive Fe-based NPs during the pyrolysis process. Moreover, the nitrogen element in the PANI-derived N-doped carbon could be behaved as a metal trapper to capture the escaped iron from Fe-TCPP units and stabilize Fe- species. Benefiting from the introduced PANI, the PANI@PCN-224(Fe)-900 has abundant single-atom Fe- sites, high content of nitrogen, large surface area, and good conductivity. Thanks to the above-mentioned unique features, PANI@PCN-224(Fe)-900 turns out to be one of the most excellent ORR catalyst in both alkaline and acidic electrolyte, even surpassing commercial Pt/C. Our work opens a new avenue to prepare single-atom metal catalysts for boosting their electrocatalytic performances in practical energy storage and conversion applications.
4. Materials and Methods
4.1. Synthesis of Catalysts
Synthesis of PCN-224(Fe). H2TCPP  and the nanoscale PCN-224  were prepared according to the literatures. The nanoscale PCN-224(Fe) was prepared by a postsynthesis method based on the reported procedure . Typically, the nanoscale PCN-224 (200 mg) and 500 mg FeCl2·4H2O were dispersed in DMF and heated at 120°C with stirring for 12 h. After that, the mixture was centrifuged and washed with fresh DMF, acetone twice, respectively. After removing acetone, the sample was dried in an oven at 70°C for 6 h. The whole process was tracked by PXRD.
Synthesis of PANI@PCN-224(Fe). The nanoscale PCN-224(Fe) (300 mg) was degassed in a Schlenk vial for 12 h at 150°C. Then, aniline hydrochloride (200 mg) dissolved in H2O (1 mL) was introduced and sonicated for 15 min. The Schlenk vial was then kept in refrigerator (ca. 4°C) for different duration time (5 h and 12 h). After that, 8 mL diluted H2O2 (0.02 M) was added dropwise into the Schlenk vial and kept under stirring at 0°C for 24 h. Then the product was obtained by centrifugation and washing with acetone for 5 times. Finally, the composite denoted as X-PANI@PCN-224(Fe) was dried under vacuum overnight, where X is the mass fraction of PANI in PCN-224(Fe) which varied from 15% to 27% depending on adsorption time (5 h and 12 h, respectively). X was determined by weighing the extracted isolated PANI from X-PANI@PCN-224(Fe). For convenience, PANI@PCN-224(Fe) was referred as 27%-PANI@PCN-224(Fe) in this article.
Preparation of Isolated PANI. The PANI in X-PANI@PCN-224(Fe) was extracted out by successively immersing the X-PANI@PCN-224(Fe) composite powder in aqueous NaOH solution (2 M) for 12 h and obtained by rinsing with water and dried under vacuum at 120°C.
Preparation of PCN-224-900, PCN-224(Fe)-900, PANI@PCN-224(Fe)-900, and PANI-900. A typical procedure was as follows: X-PANI@PCN-224(Fe) (X = 15%, 27%) powder (200 mg) was placed in a ceramic boat and transferred to a tube furnace, then heated to 200°C with a heating rate of 5°C min−1 and remained at 200°C for 2 h, then heated to 900°C with a heating rate of 5°C min−1, and calcined for 2 h at 900°C under nitrogen. After that, to remove the formed ZrO2 in the carbonaceous material, the calcined sample was etched using 5% HF solution three times at room temperature for 12 h and washed thoroughly with water and ethanol, respectively. The obtained sample was dried in vacuum at 120°C for 12 h before use. The as-prepared samples were designated as X-PANI@PCN-224(Fe)-900 (X = 15%, 27%). For convenience, PANI@PCN-224(Fe)-900 was referred as 27%-PANI@ PCN-224(Fe)-900 in this article. The PCN-224-900, PCN-224(Fe)-900, and PANI-900 samples were prepared as the same procedure except using PCN-224, PCN-224(Fe), and the isolated PANI as precursors, respectively.
4.2. Oxygen Reduction Reaction (ORR) Measurements
All the electrochemical experiments were carried out on an IM6ex (Zahner, Germany) electrochemical station. Typically, 5 mg of the catalyst and 40 μL Nafion (5% in lower ahatic alcohols and water) were dispersed in 1 mL ethanol under ultrasonication for 60 min. Then the as-prepared catalyst ink (5 μL) was dropped onto the surface of a rotating disk electrode (RDE) with a glassy carbon (GC) disk of 5 mm in diameter, after dried in air, the operation was repeated 3 times; totally 20 μL ink was dropped on GC disk. The commercial 20 wt% Pt/C (Alfa Aesar) electrode was prepared by dispersing 2.5 mg of the catalyst in 1 mL deionized water and totally 20 μL ink was dropped on GC disk. All electrochemical measurements were performed in a conventional three-electrode setup with RDE of 5 mm in diameter coated with catalysts as the working electrode, an Ag/AgCl electrode as the reference electrode and a graphite rod as the counter-electrode in 0.1 M KOH or HClO4 electrolyte. Prior to the electrochemical measurements, the electrolyte solution was saturated with O2 by bubbling O2 for 30 min. In order to ensure the O2 saturation, the O2 flow was maintained during the measurements. The polarization curves were recorded after 20 cycles of cyclic voltammetry (CV) curves with a scan rate of 10 mV·s−1. For RRDE measurements, the ring-disk electrode was scanned at a rate of 10 mV·s−1 and the ring potential was constant at 0.5 V (0.1 M KOH electrolyte), 1.2 V (0.1 M HClO4 electrolyte) vs. RHE. The electron transfer number (n) was determined with the following equations:where Id is the disk current, Ir is the ring current, and N = 0.4 is the current collection efficiency of the Pt ring.
All data needed to evaluate the conclusions in the paper are present in the paper and the Supplementary Materials. Additional data related to this paper may be requested from the authors.
Conflicts of Interest
The authors declare no competing financial interest.
Rong Cao and Yuan-Biao Huang supervised the research. Yuan-Biao Huang and Dong-Li Meng designed the experiment and wrote the paper. Dong-Li Meng and Chun-Hui Chen synthesized the materials. Dong-Li Meng performed the catalyst characterizations and catalytic experiments. Rong Cao, Yuan-Biao Huang, Dong-Li Meng, Chun-Hui Chen, Jun Liang, Qiao Wu, and Jun-Dong Yi contributed to scientific discussion of the article.
We acknowledge the financial support from the National Key Research and Development Program of China (2018YFA0208600 and 2017YFA0700100), Key Research Program of Frontier Science, CAS (QYZDJ-SSW-SLH045), Strategic Priority Research Program of the Chinese Academy of Sciences (XDB20000000), NSFC (21671188, 21871263, and 21520102001), Youth Innovation Promotion Association, CAS (2014265), and China Postdoctoral Science Found (Grant No. 2017M622089). We thank the beamline BL14W1 station for XAFS measurements at the Shanghai Synchrotron Radiation Facility, China. We thank Jing Shi and Jun Luo from University of Technology, Tianjin, for performing HAADF-STEM measurements.
S1: materials and instrumentation. Figure S1: schematic illustration of synthesis of PANI@PCN-224(Fe)-900 and PCN-224(Fe)-900 catalysts. Figure S2: (a) N2 adsorption-desorption isotherms and (b) the pore size distribution (PSD) profiles of PCN-224(Fe) and PANI@PCN-224(Fe) based on NL-DFT method. Figure S3: FT-IR spectra of PANI, PCN-224(Fe), and PANI@PCN-224(Fe). Figure S4: UV-Vis spectra of PANI, PANI@PCN-224(Fe), and PCN-224(Fe). Figure S5: PXRD of PCN-224(Fe)-900 and PANI@PCN-224(Fe)-900 before acid etching. Figure S6: Nyquist plots of PANI-900, X-PANI@PCN-224(Fe)-900, and PCN-224(Fe)-900 over the frequency range from 100 kHz to 10 mHz. Figure S7: the pore size distribution (PSD) profiles of PCN-224(Fe)-900 and PANI@PCN-224(Fe)-900 based on NL-DFT method. Figure S8: the TEM images of (a) PCN-224(Fe)-900, (b) PANI-900, and (c) 15%-PANI@PCN-224(Fe)-900. Figure S9: high-resolution TEM (HRTEM) of PANI@PCN-224(Fe)-900. Figure S10: the survey XPS spectra of PANI-900, PCN-224(Fe)-900, 15% PANI@PCN-224(Fe)-900, and PANI@PCN-224(Fe)-900. Figure S11: high-resolution N 1s spectra of (a) PANI-900 and (b) PCN-224(Fe)-900. (c) High-resolution Fe 2p spectra of PANI@PCN-224(Fe)-900. (d) Total nitrogen content of different samples. Figure S12: high-resolution N 1s spectra of (a) 15%-PANI@PCN-224(Fe)-900 and (b) PANI@PCN-224(Fe)-900. (c) Nitrogen configurations of 15%-PANI@PCN-224(Fe)-900 and PANI@PCN-224(Fe)-900. Figure S13: methanol-crossover effects test of PANI@PCN-224(Fe)-900 and Pt/C in 0.1 M KOH. Figure S14: electron transfer number of different samples obtained from the RRDE curves 0.1 M HClO4. Figure S15: methanol-crossover effects test of PANI@PCN-224(Fe)-900 and Pt/C in 0.1 M HClO4. Figure S16: LSVs of PCN-224-900, PCN-224(Fe)-900, and PANI@PCN-224(Fe)-900 in (a) 0.1 M KOH and (b) 0.1 M HClO4. Table S1: the N contents of various samples obtained through elemental analysis (EA). Table S2: the Fe contents of various samples obtained through inductively coupled plasma atomic emission spectroscopy (ICP-AES) analysis. Table S3: comparison of ORR catalytic performances in 0.1M KOH between PANI@PCN-224(Fe)-900 and other noble-metal-free electrocatalysts. Table S4: comparison of ORR catalytic performances in 0.1M HClO4 between PANI@PCN-224(Fe)-900 and other noble-metal-free electrocatalysts. (Supplementary Materials)
- E. H. Ang, K. N. Dinh, X. Sun et al., “Highly efficient and stable hydrogen production in all ph range by two-dimensional structured metal-doped tungsten semicarbides,” Research, vol. 2019, Article ID 4029516, 14 pages, 2019.
- L. Lin, W. Lei, S. Zhang, Y. Liu, G. G. Wallace, and J. Chen, “Two-dimensional transition metal dichalcogenides in supercapacitors and secondary batteries,” Energy Storage Materials, vol. 19, pp. 408–423, 2019.
- J. Sun, H. Yin, P. Liu et al., “Molecular engineering of Ni–/Co–porphyrin multilayers on reduced graphene oxide sheets as bifunctional catalysts for oxygen evolution and oxygen reduction reactions,” Chemical Science, vol. 7, no. 9, pp. 5640–5646, 2016.
- X. Yan, Y. Jia, and X. Yao, “Defects on carbons for electrocatalytic oxygen reduction,” Chemical Society Reviews, vol. 47, no. 20, pp. 7628–7658, 2018.
- B. Li, X. Chen, X. Chen et al., “Favorable lithium nucleation on lithiophilic framework porphyrin for dendrite-free lithium metal anodes,” Research, vol. 2019, Article ID 4608940, 11 pages, 2019.
- Y. Zheng, J. Han, L. Takele et al., “Poly-phenylenediamine-derived atomically dispersed Ni sites for the electroreduction of CO2 to CO,” Inorganic Chemistry Frontiers, vol. 6, no. 7, pp. 1729–1734, 2019.
- M. Shao, Q. Chang, J. Dodelet, and R. Chenitz, “Recent advances in electrocatalysts for oxygen reduction reaction,” Chemical Reviews, vol. 116, no. 6, pp. 3594–3657, 2016.
- L. Dai, Y. Xue, L. Qu, H.-J. Choi, and J.-B. Baek, “Metal-free catalysts for oxygen reduction reaction,” Chemical Reviews, vol. 115, no. 11, pp. 4823–4892, 2015.
- Y. P. Zhu, C. Guo, Y. Zheng, and S. Qiao, “Surface and interface engineering of noble-metal-free electrocatalysts for efficient energy conversion processes,” Accounts of Chemical Research, vol. 50, no. 4, pp. 915–923, 2017.
- B. P. Setzler, Z. Zhuang, J. A. Wittkopf, and Y. Yan, “Activity targets for nanostructured platinum-group-metal-free catalysts in hydroxide exchange membrane fuel cells,” Nature Nanotechnology, vol. 11, no. 12, pp. 1020–1025, 2016.
- Y. Nie, L. Li, and Z. Wei, “Recent advancements in Pt and Pt-free catalysts for oxygen reduction reaction,” Chemical Society Reviews, vol. 44, no. 8, pp. 2168–2201, 2015.
- K. Strickland, E. Miner, Q. Jia et al., “Highly active oxygen reduction non-platinum group metal electrocatalyst without direct metal–nitrogen coordination,” Nature Communications, vol. 6, no. 1, Article ID 7343, 2015.
- M. Qiao, S. S. Meysami, G. A. Ferrero et al., “Low-cost chitosan-derived n-doped carbons boost electrocatalytic activity of multiwall carbon nanotubes,” Advanced Functional Materials, vol. 28, no. 16, Article ID 1707284, 2018.
- M. Khalid, A. M. Honorato, H. Varela, and L. Dai, “Multifunctional electrocatalysts derived from conducting polymer and metal organic framework complexes,” Nano Energy, vol. 45, pp. 127–135, 2018.
- J. Guo, X. Yan, Q. Liu et al., “The synthesis and synergistic catalysis of iron phthalocyanine and its graphene-based axial complex for enhanced oxygen reduction,” Nano Energy, vol. 46, pp. 347–355, 2018.
- R. Jiang, L. Li, T. Sheng, G. Hu, Y. Chen, and L. Wang, “Edge-site engineering of atomically dispersed Fe-N4 by selective C-N bond cleavage for enhanced oxygen reduction reaction activities,” Journal of the American Chemical Society, vol. 140, no. 37, pp. 11594–11598, 2018.
- Z. Liang, X. Fan, H. Lei et al., “Cobalt-nitrogen-doped helical carbonaceous nanotubes as a class of efficient electrocatalysts for the oxygen reduction reaction,” Angewandte Chemie-International Edition, vol. 57, no. 40, pp. 13187–13191, 2018.
- C. Yang, H. Jin, C. Cui et al., “Nitrogen and sulfur co-doped porous carbon sheets for energy storage and pH-universal oxygen reduction reaction,” Nano Energy, vol. 54, pp. 192–199, 2018.
- S. Kim, J. Mahmood, C. Kim et al., “Defect-free encapsulation of Fe0 in 2D fused organic networks as a durable oxygen reduction electrocatalyst,” Journal of the American Chemical Society, vol. 140, no. 5, pp. 1737–1742, 2018.
- K. Liu, G. Wu, and G. Wang, “Role of local carbon structure surrounding fen4sites in boosting the catalytic activity for oxygen reduction,” The Journal of Physical Chemistry C, vol. 121, no. 21, pp. 11319–11324, 2017.
- W. Zhao, K. Huang, Q. Zhang et al., “In-situ synthesis, operation and regeneration of nanoporous silver with high performance toward oxygen reduction reaction,” Nano Energy, vol. 58, pp. 69–77, 2019.
- S. H. Lee, J. Kim, D. Y. Chung et al., “Design principle of Fe-N-C electrocatalysts: how to optimize multimodal porous structures?” Journal of the American Chemical Society, vol. 141, no. 5, pp. 2035–2045, 2019.
- J. Sun, S. E. Lowe, L. Zhang et al., “Ultrathin nitrogen-doped holey carbon@graphene bifunctional electrocatalyst for oxygen reduction and evolution reactions in alkaline and acidic media,” Angewandte Chemie-International Edition, vol. 57, no. 50, pp. 16511–16515, 2018.
- H. Tang, H. Yin, J. Wang, N. Yang, D. Wang, and Z. Tang, “Molecular architecture of cobalt porphyrin multilayers on reduced graphene oxide sheets for high-performance oxygen reduction reaction,” Angewandte Chemie International Edition, vol. 52, no. 21, pp. 5585–5589, 2013.
- Y. Chen, S. Ji, Y. Wang et al., “Isolated single iron atoms anchored on n-doped porous carbon as an efficient electrocatalyst for the oxygen reduction reaction,” Angewandte Chemie International Edition, vol. 56, no. 24, pp. 6937–6941, 2017.
- J. Yi, R. Xu, Q. Wu et al., “Atomically dispersed iron–nitrogen active sites within porphyrinic triazine-based frameworks for oxygen reduction reaction in both alkaline and acidic media,” ACS Energy Letters, vol. 3, no. 4, pp. 883–889, 2018.
- W. Jiang, L. Gu, L. Li et al., “Understanding the high activity of Fe-N-C electrocatalysts in oxygen reduction: Fe/Fe3C nanoparticles boost the activity of Fe-Nx,” Journal of the American Chemical Society, vol. 138, no. 10, pp. 3570–3578, 2016.
- L. Jiao, G. Wan, R. Zhang, H. Zhou, S.-H. Yu, and H.-L. Jiang, “From metal-organic frameworks to single-atom Fe implanted N-doped porous carbons: efficient oxygen reduction in both alkaline and acidic media,” Angewandte Chemie International Edition, vol. 57, no. 28, pp. 8525–8529, 2018.
- Y. Ye, H. Li, F. Cai et al., “Two-dimensional mesoporous carbon doped with Fe–N active sites for efficient oxygen Reduction,” ACS Catalysis, vol. 7, no. 11, pp. 7638–7646, 2017.
- K. Yuan, S. Sfaelou, M. Qiu et al., “Synergetic contribution of boron and Fe-Nx species in porous carbons toward efficient electrocatalysts for oxygen reduction reaction,” ACS Energy Letters, vol. 3, no. 1, pp. 252–260, 2017.
- Q. Lai, L. Zheng, Y. Liang, J. He, J. Zhao, and J. Chen, “Metal–organic-framework-derived Fe-N/C electrocatalyst with five-coordinated Fe-Nx sites for advanced oxygen reduction in acid media,” ACS Catalysis, vol. 7, no. 3, pp. 1655–1663, 2017.
- H. Zhang, S. Hwang, M. Wang et al., “Single atomic iron catalysts for oxygen reduction in acidic media: particle size control and thermal activation,” Journal of the American Chemical Society, vol. 139, no. 40, pp. 14143–14149, 2017.
- Q. Zhu, W. Xia, L. Zheng, R. Zou, Z. Liu, and Q. Xu, “Atomically dispersed Fe/N-doped hierarchical carbon architectures derived from a metal–organic framework composite for extremely efficient electrocatalysis,” ACS Energy Letters, vol. 2, no. 2, pp. 504–511, 2017.
- Q. Wang, Z. Zhou, Y. Lai et al., “Phenylenediamine-based FeNx/C catalyst with high activity for oxygen reduction in acid medium and its active-site probing,” Journal of the American Chemical Society, vol. 136, no. 31, pp. 10882–10885, 2014.
- W. Wei, X. Shi, P. Gao et al., “Well-elaborated, mechanochemically synthesized Fe-TPP⊂ZIF precursors (Fe-TPP = tetraphenylporphine iron) to atomically dispersed iron–nitrogen species for oxygen reduction reaction and Zn-air batteries,” Nano Energy, vol. 52, pp. 29–37, 2018.
- Z. Liu, F. Sun, L. Gu et al., “Post iron decoration of mesoporous nitrogen-doped carbon spheres for efficient electrochemical oxygen reduction,” Advanced Energy Materials, vol. 7, no. 22, Article ID 1701154, 2017.
- G. Wu, C. M. Johnston, N. H. Mack et al., “Synthesis–structure–performance correlation for polyaniline–Me–C non-precious metal cathode catalysts for oxygen reduction in fuel cells,” Journal of Materials Chemistry, vol. 21, no. 30, pp. 11392–11405, 2011.
- G. Wu, K. L. More, C. M. Johnston, and P. Zelenay, “High-performance electrocatalysts for oxygen reduction derived from polyaniline, iron, and cobalt,” Science, vol. 332, no. 6028, pp. 443–447, 2011.
- S. Yuan, J. Qin, J. Li et al., “Retrosynthesis of multi-component metal−organic frameworks,” Nature Communications, vol. 9, no. 1, Article ID 808, 2018.
- J. Liang, Y. Huang, and R. Cao, “Metal–organic frameworks and porous organic polymers for sustainable fixation of carbon dioxide into cyclic carbonates,” Coordination Chemistry Reviews, vol. 378, pp. 32–65, 2019.
- G. Chen, Y. Yu, X. Wu et al., “Microfluidic electrospray niacin metal-organic frameworks encapsulated microcapsules for wound healing,” Research, vol. 2019, Article ID 6175398, 11 pages, 2019.
- Y. Hu, X. Xu, B. Zheng et al., “Functional macro-microporous metal-organic frameworks for improving the catalytic performance,” Small Methods, vol. 3, no. 5, Article ID 1800547, 2019.
- A. Mahmood, W. Guo, H. Tabassum, and R. Zou, “Metal-organic framework-based nanomaterials for electrocatalysis,” Advanced Energy Materials, vol. 6, no. 17, Article ID 1600423, 2016.
- C. Zhang, B. Lu, F. Cao et al., “Electrospun metal-organic framework nanoparticle fibers and their derived electrocatalysts for oxygen reduction reaction,” Nano Energy, vol. 55, pp. 226–233, 2019.
- Y. Chu, L. Guo, B. Xi et al., “Embedding MnO@Mn3O4 nanoparticles in an N-doped-carbon framework derived from Mn-organic clusters for efficient lithium storage,” Advanced Materials, vol. 30, no. 6, Article ID 1704244, 2018.
- W. Ahn, M. G. Park, D. U. Lee et al., “Hollow multivoid nanocuboids derived from ternary Ni–Co–Fe prussian blue analog for dual-electrocatalysis of oxygen and hydrogen evolution reactions,” Advanced Functional Materials, vol. 28, no. 28, Article ID 1802129, 2018.
- F. Xiao, G. Xu, C. Sun et al., “Nitrogen-coordinated single iron atom catalysts derived from metal organic frameworks for oxygen reduction reaction,” Nano Energy, vol. 61, pp. 60–68, 2019.
- S. Zhao, H. Yin, L. Du et al., “Carbonized nanoscale metal–organic frameworks as high performance electrocatalyst for oxygen reduction reaction,” ACS Nano, vol. 8, no. 12, pp. 12660–12668, 2014.
- S. You, X. Gong, W. Wang et al., “Enhanced cathodic oxygen reduction and power production of microbial fuel cell based on noble-metal-free electrocatalyst derived from metal-organic frameworks,” Advanced Energy Materials, vol. 6, no. 1, Article ID 1501497, 2016.
- D. Feng, W. Chung, Z. Wei et al., “Construction of ultrastable porphyrin Zr metal–organic frameworks through linker elimination,” Journal of the American Chemical Society, vol. 135, no. 45, pp. 17105–17110, 2013.
- J. Stejskal, P. Kratochvíl, and A. D. Jenkins, “Polyaniline: forms and formation,” Collection of Czechoslovak Chemical Communications, vol. 60, no. 10, pp. 1747–1755, 1995.
- D. Strmcnik, D. Li, P. P. Lopes et al., “When small is big: the role of impurities in electrocatalysis,” Topics in Catalysis, vol. 58, no. 18-20, pp. 1174–1180, 2015.
- W. Liu, J. Kumar, S. Tripathy, K. J. Senecal, and L. Samuelson, “Enzymatically synthesized conducting polyaniline,” Journal of the American Chemical Society, vol. 121, no. 1, pp. 71–78, 1999.
- A. Pron and P. Rannou, “Processible conjugated polymers: From organic semiconductors to organic metals and superconductors,” Progress in Polymer Science, vol. 27, no. 1, pp. 135–190, 2002.
- C. Xuan, B. Hou, W. Xia et al., “From a ZIF-8 polyhedron to three-dimensional nitrogen doped hierarchical porous carbon: an efficient electrocatalyst for the oxygen reduction reaction,” Journal of Materials Chemistry A, vol. 6, no. 23, pp. 10731–10739, 2018.
- L. Wang, X. Feng, L. Ren et al., “Flexible solid-state supercapacitor based on a metal–organic framework interwoven by electrochemically-deposited PANI,” Journal of the American Chemical Society, vol. 137, no. 15, pp. 4920–4923, 2015.
- J. Yang, X. Wang, B. Li et al., “Novel iron/cobalt-containing polypyrrole hydrogel-derived trifunctional electrocatalyst for self-powered overall water splitting,” Advanced Functional Materials, vol. 27, no. 17, Article ID 1606497, 2017.
- B. Wang, X. Wang, J. Zou et al., “Simple-cubic carbon frameworks with atomically dispersed iron dopants toward high-efficiency oxygen reduction,” Nano Letters, vol. 17, no. 3, pp. 2003–2009, 2017.
- Q. Li, W. Chen, H. Xiao et al., “Fe isolated single atoms on S, N codoped carbon by copolymer pyrolysis strategy for highly efficient oxygen reduction reaction,” Advanced Materials, vol. 30, no. 25, Article ID 1800588, 2018.
- H.-W. Liang, W. Wei, Z.-S. Wu, X. Feng, and K. Müllen, “Mesoporous metal-nitrogen-doped carbon electrocatalysts for highly efficient oxygen reduction reaction,” Journal of the American Chemical Society, vol. 135, no. 43, pp. 16002–16005, 2013.
- W. Ding, L. Li, K. Xiong et al., “Shape fixing via salt recrystallization: a morphology-controlled approach to convert nanostructured polymer to carbon nanomaterial as a highly active catalyst for oxygen reduction reaction,” Journal of the American Chemical Society, vol. 137, no. 16, pp. 5414–5420, 2015.
- H. Peng, F. Liu, X. Liu et al., “Effect of transition metals on the structure and performance of the doped carbon catalysts derived from polyaniline and melamine for orr application,” ACS Catalysis, vol. 4, no. 10, pp. 3797–3805, 2014.
- W. Niu, L. Li, X. Liu et al., “Mesoporous n-doped carbons prepared with thermally removable nanoparticle templates: an efficient electrocatalyst for oxygen reduction reaction,” Journal of the American Chemical Society, vol. 137, no. 16, pp. 5555–5562, 2015.
- A. Zitolo, V. Goellner, V. Armel et al., “Identification of catalytic sites for oxygen reduction in iron- and nitrogen-doped graphene materials,” Nature Materials, vol. 14, no. 9, pp. 937–942, 2015.
- X. Chen, L. Yu, S. Wang, D. Deng, and X. Bao, “Highly active and stable single iron site confined in graphene nanosheets for oxygen reduction reaction,” Nano Energy, vol. 32, pp. 353–358, 2017.
- P. Chen, T. Zhou, L. Xing et al., “Atomically dispersed iron–nitrogen species as electrocatalysts for bifunctional oxygen evolution and reduction reactions,” Angewandte Chemie International Edition, vol. 56, no. 2, pp. 610–614, 2017.
- Q. Jia, N. Ramaswamy, H. Hafiz et al., “Experimental observation of redox-induced Fe–N switching behavior as a determinant role for oxygen reduction activity,” ACS Nano, vol. 9, no. 12, pp. 12496–12505, 2015.
- Q. Liu, X. Liu, L. Zheng, and J. Shui, “The solid-phase synthesis of an Fe-N-C electrocatalyst for high-power proton-exchange membrane fuel cells,” Angewandte Chemie International Edition, vol. 57, no. 5, pp. 1204–1208, 2018.
- D. W. Feng, Z. Y. Gu, J. R. Li, H. L. Jiang, Z. W. Wei, and H. C. Zhou, “Zirconium-metalloporphyrin PCN-222: mesoporous metal-organic frameworks with ultrahigh stability as biomimetic catalysts,” Angewandte Chemie, vol. 51, no. 41, pp. 10307–10310, 2012.
- J. Park, Q. Jiang, D. Feng, L. Mao, and H. Zhou, “Size-controlled synthesis of porphyrinic metal–organic framework and functionalization for targeted photodynamic therapy,” Journal of the American Chemical Society, vol. 138, no. 10, pp. 3518–3525, 2016.
Copyright © 2019 Dong-Li Meng et al. Exclusive licensee Science and Technology Review Publishing House. Distributed under a Creative Commons Attribution License (CC BY 4.0).