Ultrafast Synthesis of Calcium Vanadate for Superior Aqueous Calcium-Ion Battery

Figure 1

Realistic and schematic representation of the molten salt method synthesis process. (a) The precursor was added when salts were heated to the molten state. (b) The sample was removed from the furnace after reacting for a few minutes. (c) The samples were obtained after washing with DI water.