Research Article | Open Access
Jian Li, Zhiguang Guo, "Patterned Slippery Surface for Bubble Directional Transportation and Collection Fabricated via a Facile Method", Research, vol. 2019, Article ID 9139535, 9 pages, 2019. https://doi.org/10.34133/2019/9139535
Patterned Slippery Surface for Bubble Directional Transportation and Collection Fabricated via a Facile Method
Directional manipulation of underwater bubbles on a solid surface has attracted much attention due to its large-scale applications such as electrocatalytic gas evolution reactions, wastewater remediation, and solar energy harvesting. In this work, the patterned slippery surface (PSS) is fabricated via a facile method where the patterned pathways are fabricated by means of etching the pristine copper sheet. These patterned surfaces consisted of pristine copper and modified oxide copper which exhibit different wettability for bubble and water. The superhydrophobic and aerophilic surface can efficiently capture bubbles, and the infused oil layer is beneficial for reducing the resistance during transportation. Furthermore, the bubble can move upward, downward, and horizontally. Hence, it is easy to realize the bubble’s transportation and collection on the functional surfaces.
The manipulation of underwater bubbles is significant in a fluid system due to its large-scale applications, such as electrocatalytic gas evolution reactions, wastewater remediation, and solar energy harvesting [1–11]. Meanwhile, the bubbles play an important role in nature. For instance, the superhydrophobic abdomen of diving bell spiders can capture bubbles for its further living in the water [12, 13]. However, the underwater bubbles also have some negative effects in industries, such as corrosion of pipes, air locks, and clogging of bubbles in intravenous tubing [14–18]. Thus, it is urgent to spend further time in research for bubble’s capture and removal. In addition, there are significant correlations between liquid wettability and bubble wettability which have been reported in recent years [19–21]. The three-phase (gas-liquid-solid) contact line of bubble on a solid surface in an aqueous environment is the same as water droplet on the solid surface in air. For an ideal surface, the bubble contact angle is complementary to water contact angle. Therefore, the superhydrophobic surface presents as aerophilic while the hydrophilic surface is aerophobic. Bubbles can be captured more easily on the superhydrophobic surface than on the superhydrophilic surface.
Thus, surfaces with the super wetting ability can be applied in bubble manipulation. Tian et al.  have fabricated superhydrophobic PE plates with modified nanoparticles coated on it. Releasing continuous bubbles on the plate underwater, it can float and dive with bubble capture and breakage. It manifested that the superhydrophobic layer could capture bubbles efficiently, and bubbles could merge into a larger one. Yu et al.  realized the directional manipulation of bubbles on a superhydrophobic helix. The bubble stayed on the climax of the helix under the coeffect of buoyancy and adherence and moved directionally along the helix when it rotated. In addition, they also realized the spontaneous directional transportation of bubbles on a superhydrophobic cone . In general, there is a high adhesive force between the superhydrophobic substrate and bubbles. Bubbles tend to spread rapidly and adhere to the surface due to the interaction of air and substrates [25–27]. Inspired by the movement of water droplets or insects on Pitcher plant, spider silk, and cactus spine [28–33], the slippery surfaces with a lubricant layer and the substrates with a geometrical gradient have been applied largely in the directional manipulation of underwater bubbles [7, 10, 34–41]. Zhang et al.  designed a wedge-shaped superhydrophobic surface with a lubricant layer via laser cutting for this directional movement. This movement occurred in a horizontal direction in which bubbles suffered unbalanced Laplace pressure, and the bubble moves entirely rather than pinned on the surface. Additionally, Tang et al.  used photolithograph to manufacture bioinspired patterned slippery surface which achieved upward directional transportation of buoyancy-driven bubbles. Furthermore, the directional transportation of bubbles can also be realized on the Janus membrane where bubbles can only penetrate from the hydrophilic side to the hydrophobic side [42–44]. Yin et al.  realized the bubble transportation through a Janus PFTE mesh which was created via a femtosecond laser. As mentioned above, the driving force for this transportation mainly depends on buoyancy and unbalanced Laplace pressure. Though there are many surfaces which are served for bubble directional transportation, the most fabricated methods are complex and time-consuming, such as laser cutting and photolithograph [24, 34, 39, 42, 43]. Thus, it is significant to explore a facile method to fabricate a functional surface for directional transportation.
Herein, a facile method has been presented in this work for fabricating the patterned slippery surfaces (PSS) for bubble manipulation. Patterns were fabricated by covering a part of the copper substrate with tape when etching. Besides, the pattern can be designed by adjusting the shape of the tape. With different shapes on the slippery surface, the manipulations of bubble can be controlled. Furthermore, bubbles can move upward with different paths by buoyancy, horizontal and downward on PSS with geometrical gradient under unbalanced Laplace pressure. This facile method is beneficial for further study of bubble manipulation.
2. Result and Discussion
2.1. Preparation of Patterned Slippery Surface and Characterization
The etching process was expressed as previous work . The whole fabrication process of this patterned slippery surface was shown in Figure 1. The transparent tape was functional for the protection to avoid pristine copper to be etched which resulted in a patterned surface, the yellow part reflected the pristine copper, and the black part meant the oxide copper after being etched. Figures 1(a)–1(c) show the detailed morphologies of the modified oxide copper and the section view of the patterned surface. The oxide copper showed a spherical shape, and the section view displayed a concave-convex shape. The oxide copper was in the lower part. Besides, the width ratio between the yellow and black parts is 1 : 1. Furthermore, the images of bubble and water contact angles on different types of surfaces (superhydrophobic surfaces, slippery surfaces, original surfaces, and PSS) were shown in Figure 2, Figure S1, and Table S1. In addition, the black part was modified to be superhydrophobic and aerophilic with the water and bubble contact angles of and ; the pristine copper is hydrophilic and aerophobic of water and bubble contact angles of and . For the ideal surface, the water contact angle () in air and the bubble contact angle () in water complementary resulted from almost the same three-phase contact line. Additionally, the effect of buoyancy for bubble was analogous of gravity for water droplet. According to Young’s equation, the values of and can be calculated as where , , and represented the surface energy of solid-vapor interface, liquid-vapor interface, and solid-liquid interface, respectively. Based on equation (1) and (2), it is easy to derive . After lubricant PFPE was infused, the oil layer had substituted the solid substrate which resulted in the change of three phases. Therefore, the water (θwo) and bubble (θbo) contact angles were and with oil layer, which can be expressed as where and are the surface energy of oil-vapor interface and oil-liquid phase. Besides, θwo and θwb were still complementary, . In addition, the patterned surface displays anisotropic wettability that resulted from the wettability difference between the yellow and black parts; the bubble contact angle is and in the and directions on the treated part with 1 mm width. From these results, it can be concluded that the treated part remains aerophilic for better bubble capture and transportation.
2.2. Directional Manipulation of Bubble on PSS with Straight Stripes
As for the whole process of bubble directional manipulation, the first step is capturing the bubbles. As shown in Figure 3(a), the pristine copper sheet cannot capture bubbles. Bubbles bounced to the upper position continuously to escape after it contacted with the inclined samples since the pristine copper is aerophobic. Moreover, the directional manipulation of underwater bubbles cannot be realized on the superhydrophobic oxide copper. From Figure 3(b), the silver mirror-like phenomenon was observed immediately on the superhydrophobic sample after being immersed in water; there was a bubble layer on the sample. Additionally, although the substrate can capture bubbles efficiently, bubbles stay in the original position to expand the air layer instead of moving upward, which was shown in Figure 3(b). Thus, it is hard to realize the directional transportation of underwater bubbles on superhydrophobic substrates, while in previous work the directional transportation of bubbles has been accomplished by a slippery surface with shape gradient structure .
Therefore, based on those researches, the slippery surface fabricated by the superhydrophobic substrate with infused oil layer was conducive to capture and transport bubbles [25, 34–37, 39]. In this work, we have fabricated patterned slippery surface (PSS) with different widths to achieve the goal of directional manipulation. As shown in Figure 4 and Movie S1, the PSS-2 was inclined in water to observe the bubble movement. Then, releasing a single bubble with the volume of about 15 μL in the slippery stripe, it was restricted by the boundary on the treated stripes and moved from the bottom up with the shape of ellipse (Figure 4(a)). Besides, releasing a single bubble with the same volume in the untreated stripe, the bubble bounced on the stripe to the upper location firstly, then it moved horizontally to the slippery area that resulted from the touch between the bubble and the slippery stripe. Then, the bubble transported to the top on the slippery stripe after horizontal movement (Figure 4(b)). From the single bubble motion on the PSS-2, it can be concluded that the combined surface can realize the directional manipulation of underwater bubbles on the treated stripes. Further, the same phenomenon had been observed in samples of PSS-1 and PSS-3 as shown in Fig. S2 and S3 with the same volume of bubble. Bubbles appeared in different shapes in treated stripes with different widths that resulted from the tendency that bubble would cover more area on the treated stripes. The transportations were also shown in Movie S1 and S2. However, there were some special phenomena in the directional manipulation in the samples PSS-1 and PSS-3 with the single bubble with the volume of 15 μL. As shown in Figure 4(c), the bubble covered three stripes (treated, untreated, and treated) during the whole upward transportation with the first contacted position of the untreated stripe, while in the sample of PSS-3 the bubble moved from the bottom up in the untreated part instead of a horizontal movement to the treated stripe to the top, which was shown in Figure 4(d). The special transportations were also shown in Movie S1. It can be ascribed to the relationship of bubble volume and stripe width. In PSS-1, the bubble tended to move horizontally to the treated part after being released on the untreated part, but the stripe width was much narrower compared to the bubble diameter that resulted in the touch between the bubble and two treated stripes. Then, the bubble and three stripes achieve a balance for directional movement. Nevertheless, the sample width of PSS-3 was too large for this bubble which resulted in the bouncing of the bubble from bottom up on the untreated stripe. From those movements of 15 μL bubble on the PSS samples, it could be concluded that the directional movement was mainly decided by the treated stripe which offered the capacity of capturing bubbles and the transport area. Furthermore, the horizontal movement depended on the contact of the bubble and the treated part. The treated part is also aerophilic with the oil layer for bubbles containing lower free energy than the pristine copper part that resulted in better capturing of the bubbles. Moreover, the added oil layer can make the substrate more regular and polisher to cover defects of this substrate. Based on this oil layer, bubbles can move entirely instead of bulk of movement with part of it remaining in the initial position under the driving force of buoyancy. In addition, the driving force for the bubble directional transportation included buoyancy () and Laplace force difference (), and the resistance was mainly generated by the adhesive force () and the sample defects (), which was shown in Figure 5. Furthermore, the buoyancy was generated by a part of the bubble which was the unbounded region, can be calculated as [46, 47] where is the density of water, is the gravitational acceleration, and VP is the effective volume of the bubble (the left part of bubble in Figure 5(b)). Moreover, there is a Laplace force difference () generated by the curved bubble surface; it can be calculated as  where is the surface tension of water, and are the radii of bubble in the front and back sides, and and are the projected area of the bubble at the front and back sides. In addition, in those inclined samples, the adhesion belonged to the lateral adhesion () which its direction is against the directional transportation of bubbles on a solid substrate [46–49]. Thus, the resultant force () in the moving direction can be calculated as where is the inclined angle of the surface in water. Based on equation (6), the movement was affected by several factors. and mainly depended on the inclined angle; had been reduced by the oil layer that resulted in the directional transportation. From above experiments, it can be confirmed that the PSS samples with straight treated stripes can realize efficiently the directional transportation of bubbles. Further, the samples also reduced the modified area in the total surface but with the same capacity of capturing bubbles compared to the whole modified surface which was beneficial for the environment. Hence, the patterned surface with the oil layer is an ideal candidate for capturing and transporting bubbles underwater.
2.3. Directional Transportation of Bubbles on PSS Samples with Special Shapes
Based on the fabricated method of the above samples with straight pathway, we also had fabricated the patterned slippery surface with the treated part displayed letter “C” (PSS-C). The width of the treated path was 4 mm. As shown in Figure 6(a), the bubble with a volume of 15 μL moved from the bottom up in a curve track which was the same as the treated path. The boundary line had played an important role in preventing the bubble escape from the treated path. Thus, the treated path on PSS samples offered the transported tracks for bubbles after bubble releasing. We also fabricated the patterned slippery surface with the treated part displayed letter “M” (PSS-M). There were some turning points in this sample. Therefore, the single bubble with the volume of about 15 μL was released on the PSS-M to detect the ability of directional transportation on this sample, which was shown in Figure 6(b) and Movie S2. The width of “M” was 3 mm, and the boundary lines were parallel and straight. The single bubble displayed a circular shape and moved along the treated path. Then, the bubble turned right and left when it reached the turning point of letter “M” in order to remain on the treated part all the time. Moreover, the shape of the bubble changed largely when going through the turning point. The transported track was also the same as the treated path, the letter “M.” With the letters “M” and “C” on the substrate, we can control the directional transportation of bubbles underwater more precisely in ideal directions and paths. Although those PSS samples (PSS-1, PSS-2, PSS-3, PSS-C, and PSS-M) could realize the directional transportations, bubbles could only move vertically from the lower position to the higher position driven by buoyancy force. Nonetheless, this facile method of fabricating the PSS samples offered the opportunity for spontaneous directional transportation of bubbles underwater. Thus, we fabricated the PSS samples with wedge shapes for spontaneous directional transportation of bubbles. There were four equal wedges on the copper sheet with the apex angle of 7°. As shown in Figure 7(a) and Movie S2, the bubble moved from the narrow tip to the wide end after being released on the wedge spontaneously. Besides, the bubble moved faster in the early time and slowed down to stagnation. Moreover, this PSS-wedge sample could also realize antibuoyancy movement. As shown in Figure 7(b) and Movie S2, the bubble moved downward spontaneously after being released on the inclined sample. The driving force on this sample of the PSS-wedge was the Laplace force difference () no matter how the bubble moved. As shown in Figure 7(c), can be calculated as [34, 50] where is the surface tension of the oil layer, is the apex angle, is the bubble volume, and and are the radii of the bubble in the tip and end positions. For the movement in Figure 7(b), the buoyancy became the resistance. Thus, the transported distance was much shorter than that in the inclined PSS-wedge sample. Hence, the patterned slippery surface can be designed with serval special shapes on it by covering the pristine copper sheet for further directional transportation of bubbles.
2.4. Bubble Transportation and Collection on PSS-Y
Bubble capture and collection have attracted much attention in recent years. Though there were many materials investigated for bubble collection, simplifying the fabrication methods for those materials was still a challenge. However, the PSS samples were fabricated via a facile etching method and it could efficiently capture bubbles and transport them along the treated area. Therefore, we designed a sample (PSS-Y) based on this method to achieve the goal of bubble collection. This sample also included two parts, the treated and untreated parts. As shown in Figure 8(a), the treated part was combined by two areas, the collect area and the transport area. Moreover, the transport area was 4 mm wide and 20 mm long which showed a rectangle, while another area showed a trapezoid with the upper and lower widths of 4 mm and 20 mm, respectively, and the height was 20 mm. The total process of bubble collection could be divided into three steps: attach on the collect area, move on to the transport area, and escape from this sample. We first examined the movement of two individual bubbles on this PSS-Y sample. As shown in Figure 8(b) and Movie S3, two bubbles with the volume of about 15 μL moved upward along the boundary line in the lower part. Then, the two bubbles merged into one when they moved to the joint between the straight and lower part. Finally, the merged bubble transported on the stripe to the end along the treated straight path. From the transportation of bubbles on the sample of PSS-Y, this special PSS samples could collect bubbles by the two parts. Based on the phenomenon of two bubbles on PSS-Y, we have released multiple bubbles on PSS-Y in different positions. From Figure 8(c) and Movie S3, all bubbles were captured by the collect area and moved along the treated part. Furthermore, bubbles might coalesce in the joint and move upward to escape this sample in the straight treated path. In this sample of PSS-Y, the trapezoid part had amplified the contact area between bubbles and sample which resulted in larger collect area, and the straight part restricted the leaving position of bubbles for bubble collection.
In summary, the directional transportation and collection of bubbles underwater were realized on the patterned slippery surfaces which were fabricated via a facile method. These samples of PSS were combined by two regions, the treated superhydrophobic part with lubricant infused and the untreated part of the pristine copper. The superhydrophobic and aerophilic surface can efficiently capture bubbles, and the infused oil layer was beneficial for reducing the resistance for bubble transportation. Hence, the samples were capable of capturing and transporting bubbles on the treated part. Further, with a well-designed path on the surface such as PSS-C, PSS-M, and PSS-wedge, the directional transportation of bubbles can be organized precisely. Furthermore, the PSS-Y can realize the bubble’s collection. This facile method demonstrated promising prospective in fabricating substrates for directional transportation and collection of bubbles.
4. Experimental Section
All reagents are obtained as listed. Pentadecafluorooctanoic acid (PFOA) was obtained from Saen Chemical Technology Co., Ltd.; hydrochloric acid (HCl) was obtained from Xilong Scientific. Ammonium persulfate (98%, (NH4)2S2O8), sodium hydroxide (96%, NaOH), ethyl alcohol, and acetone were purchased from Tianjin Rionlon Pharmaceutical Science & Technology Development Co., Ltd. Copper foils were supplied by Sinopharm Chemical Reagent Co., Ltd. The transparent tape was purchased from a local supermarket. The DuPont Krytox perfluoroalkylpolyether (PFPE, >95.0%) GPL 103 lubricant was purchased from the Chemours Company. The bubbles were generated by the syringe of air bubble. Deionized (DI) water was purified using a ModuPure system and used throughout the study.
4.2. Preparation of Patterned Slippery Surface
Copper sheet () was cleaned several times by acetone, ethanol, dilute hydrochloric acid, and deionized water under consecutive ultrasonication for about 40 minutes. Put the tapes (, , and ) on the substrate line by line with the spacing of 1 mm, 2 mm, or 3 mm after drying the substrate in an oven at 60°C. Then, put the samples into a mixed etching solution of 100 mL (2 mol/L NaOH, 0.1 mol/L (NH4)2S2O8) for 3 h to obtain CuO on the uncovered surface. After that, peel the tape to obtain the patterned surface which was combined by pristine copper and etched copper. Dry the surface by N2 and modify it by PFOA water solution (0.01 mol/L) to obtain superhydrophobicity of the treated part. At last, an amount of PFPE was applied on the patterned surfaces to realize the patterned slippery surfaces with different stripe widths (PSS-1, PSS-2, and PSS-3).
Field emission scanning electron microscope (FESEM, JSM-6701F) with Au-sputtered specimens was served to obtain detailed morphologies of the surface. The contact angles of water and bubble on serval samples were measured by a JC2000D goniometer (Zhongchen Digital Equipment Co. Ltd., Shanghai, China). All photographs and videos were captured by a mobile phone and a digital camera (Sony camera, DSCHX200). The average contact angles were measured in the same sample in five different positions.
4.4. Directional Manipulation and Collection of Bubbles
Those bubble manipulations included two types, the buoyancy-driven and the self-driven. Moreover, the positions of those samples were different. The samples for buoyancy-driven were fixed underwater vertically with an inclined angle of 40°, while the others were horizontally placed in the container. Bubbles were generated by the syringes.
Conflicts of Interest
The authors declare that there are no conflicts of interest regarding the publication of this article.
The authors received financial support for the research from the National Natural Scientific Foundation of China (Nos. 51675513 and 51735013).
Supplementary 1. Table S1: the values of water and bubble contact angles in different wetting states. Figure 1: images of water or bubble contact angles on various surfaces: (a) pristine copper, (b, c) PSS-2, and (d) PSS-3. Figure 2: directional transportation of a single bubble on PSS-1 with different initial contact position: (a) the treated stripe and (b) the untreated stripe. Figure 3: directional transportation of a single bubble on PSS-3 with different initial contact position: (a) the treated stripe and (b) the untreated stripe.
Supplementary 2. Movie 1: directional transportation of a single bubble on PSS 1, 2, and 3.
Supplementary 3. Movie 2: directional transportation of a single bubble on PSS with special shapes.
Supplementary 4. Movie 3: bubble movement on PSS-Y.
- J. Wang, Y. Zheng, F. Q. Nie, J. Zhai, and L. Jiang, “Air bubble bursting effect of lotus leaf,” Langmuir, vol. 25, no. 24, pp. 14129–14134, 2009.
- Z. Lu, W. Zhu, X. Yu et al., “Ultrahigh Hydrogen Evolution Performance of Under‐Water “Superaerophobic” MoS2 Nanostructured Electrodes,” Advanced Materials, vol. 26, no. 17, pp. 2683–2687, 2014.
- U. von Gunten, “Ozonation of drinking water: Part II. Disinfection and by-product formation in presence of bromide, iodide or chlorine,” Water Research, vol. 37, no. 7, pp. 1469–1487, 2003.
- C. Zhang, M. Cao, H. Ma et al., “Morphology-Control Strategy of the Superhydrophobic Poly(Methyl Methacrylate) Surface for Efficient Bubble Adhesion and Wastewater Remediation,” Advanced Functional Materials, vol. 27, no. 43, article 1702020, 2017.
- M. Notarianni, K. Vernon, A. Chou, M. Aljada, J. Liu, and N. Motta, “Plasmonic effect of gold nanoparticles in organic solar cells,” Solar Energy, vol. 106, pp. 23–37, 2014.
- A. Polman, “Solar steam nanobubbles,” ACS Nano, vol. 7, no. 1, pp. 15–18, 2013.
- C. Yu, M. Cao, Z. Dong et al., “Aerophilic electrode with cone shape for continuous generation and efficient collection of H2 bubbles,” Advanced Functional Materials, vol. 26, no. 37, pp. 6830–6835, 2016.
- P. Zhang, J. Zhang, Z. Xue, J. Wang, and L. Jiang, “Reliable manipulation of gas bubbles by regulating interfacial morphologies and chemical components,” Materials Horizons, vol. 4, no. 4, pp. 665–672, 2017.
- C. Yu, P. Zhang, J. Wang, and L. Jiang, “Superwettability of gas bubbles and its application: from bioinspiration to advanced materials,” Advanced Materials, vol. 29, no. 45, article 1703053, 2017.
- H. Ma, M. Cao, C. Zhang et al., “Directional and Continuous Transport of Gas Bubbles on Superaerophilic Geometry-Gradient Surfaces in Aqueous Environments,” Advanced Functional Materials, vol. 28, no. 7, article 1705091, 2018.
- Y. Jiao, C. Li, S. Wu et al., “Switchable underwater bubble wettability on laser-induced titanium multiscale micro-/nanostructures by vertically crossed scanning,” ACS Applied Materials & Interfaces, vol. 10, no. 19, pp. 16867–16873, 2018.
- N. J. Shirtcliffe, G. McHale, M. I. Newton, C. C. Perry, and F. B. Pyatt, “Plastron properties of a superhydrophobic surface,” Applied Physics Letters, vol. 89, no. 10, article 104106, 2006.
- G. O. Stride, “The Respiratory Bubble of the Aquatic Beetle, Potamodytes tuberosus, Hinton,” Nature, vol. 171, no. 4359, pp. 885-886, 1953.
- M. B. Kermani and A. Morshed, “Carbon dioxide corrosion in oil and gas production—a compendium,” Corrosion, vol. 59, no. 8, pp. 659–683, 2003.
- A. Samimi, “Studying corrosion electrochemical mechanism in tube line,” International Journal of Science and Investigations, vol. 1, pp. 32–35, 2012.
- C. Reynolds and M. Yitayew, “Low-head bubbler irrigation systems. Part II. Air lock problems,” Agricultural Water Management, vol. 29, no. 1, pp. 25–35, 1995.
- S. K. Mazloomi and N. Sulaiman, “Influencing factors of water electrolysis electrical efficiency,” Renewable and Sustainable Energy Reviews, vol. 16, no. 6, pp. 4257–4263, 2012.
- R. Hannemann, B. Hamman, and R. Barile, “Preventing bubbles in intravenous tubing,” JAMA, vol. 236, no. 22, pp. 2488-2489, 1976.
- J. E. George, S. Chidangil, and S. D. George, “Recent progress in fabricating superaerophobic and superaerophilic surfaces,” Advanced Materials Interfaces, vol. 4, no. 9, article 1601088, 2017.
- P. Zhang, S. Wang, S. Wang, and L. Jiang, “Superwetting surfaces under different media: effects of surface topography on wettability,” Small, vol. 11, no. 16, pp. 1939–1946, 2015.
- B. Liu, R. Manica, X. Zhang et al., “Dynamic Interaction between a Millimeter–Sized Bubble and Surface Microbubbles in Water,” Langmuir, vol. 34, no. 39, pp. 11667–11675, 2018.
- P. Tian, X. Gao, G. Wen, L. Zhong, Z. Wang, and Z. Guo, “Diving–floating locomotion induced by capturing and manipulating bubbles in an aqueous environment,” Chemical Communications, vol. 54, no. 83, article 11713, 11716 pages, 2018.
- C. Yu, X. Zhu, M. Cao, C. Yu, K. Li, and L. Jiang, “Superhydrophobic helix: controllable and directional bubble transport in an aqueous environment,” Journal of Materials Chemistry A, vol. 4, no. 43, article 16865, 16870 pages, 2016.
- C. Yu, M. Cao, Z. Dong, J. Wang, K. Li, and L. Jiang, “Spontaneous and directional transportation of gas bubbles on superhydrophobic cones,” Advanced Functional Materials, vol. 26, no. 19, pp. 3236–3243, 2016.
- J. Li and Z. Guo, “Bubble shapes and their changes on slippery surfaces during directional transportation,” Journal of Colloid and Interface Science, vol. 552, pp. 84–90, 2019.
- C. Shi, X. Cui, X. Zhang et al., “Interaction between air bubbles and superhydrophobic surfaces in aqueous solutions,” Langmuir, vol. 31, no. 26, pp. 7317–7327, 2015.
- L. Xie, C. Shi, X. Cui, and H. Zeng, “Surface forces and interaction mechanisms of emulsion drops and gas bubbles in complex fluids,” Langmuir, vol. 33, no. 16, pp. 3911–3925, 2017.
- J. Li and Z. Guo, “Spontaneous directional transportations of water droplets on surfaces driven by gradient structures,” Nanoscale, vol. 10, no. 29, article 13814, 13831 pages, 2018.
- U. Bauer and W. Federle, “The insect-trapping rim of Nepenthes pitchers,” Plant Signaling & Behavior, vol. 4, no. 11, pp. 1019–1023, 2009.
- H. Chen, P. Zhang, L. Zhang et al., “Continuous directional water transport on the peristome surface of Nepenthes alata,” Nature, vol. 532, no. 7597, pp. 85–89, 2016.
- J. Ju, H. Bai, Y. Zheng, T. Zhao, R. Fang, and L. Jiang, “A multi-structural and multi-functional integrated fog collection system in cactus,” Nature Communications, vol. 3, no. 1, p. 1247, 2012.
- Y. Zheng, H. Bai, Z. Huang et al., “Directional water collection on wetted spider silk,” Nature, vol. 463, no. 7281, pp. 640–643, 2010.
- T. S. Wong, S. H. Kang, S. K. Y. Tang et al., “Bioinspired self-repairing slippery surfaces with pressure-stable omniphobicity,” Nature, vol. 477, no. 7365, pp. 443–447, 2011.
- C. Zhang, B. Zhang, H. Ma et al., “Bioinspired pressure-tolerant asymmetric slippery surface for continuous self-transport of gas bubbles in aqueous environment,” ACS Nano, vol. 12, no. 2, pp. 2048–2055, 2018.
- X. Xiao, C. Zhang, H. Ma et al., “Bioinspired slippery cone for controllable manipulation of gas bubbles in low-surface-tension environment,” ACS Nano, vol. 13, no. 4, pp. 4083–4090, 2019.
- C. Yu, X. Zhu, K. Li, M. Cao, and L. Jiang, “Manipulating Bubbles in Aqueous Environment via a Lubricant-Infused Slippery Surface,” Advanced Functional Materials, vol. 27, no. 29, article 1701605, 2017.
- Y. Jiao, X. Lv, Y. Zhang et al., “Pitcher plant-bioinspired bubble slippery surface fabricated by femtosecond laser for buoyancy-driven bubble self-transport and efficient gas capture,” Nanoscale, vol. 11, no. 3, pp. 1370–1378, 2019.
- M. Chen, Z. Jia, T. Zhang, and Y. Fei, “Self-transport of underwater bubbles on a microholed hydrophobic surface with gradient wettability,” Soft Matter, vol. 14, no. 36, pp. 7462–7468, 2018.
- X. Tang, H. Xiong, T. Kong, Y. Tian, W. D. Li, and L. Wang, “Bioinspired nanostructured surfaces for on-demand bubble transportation,” ACS Applied Materials & Interfaces, vol. 10, no. 3, pp. 3029–3038, 2018.
- J. Lee, S. Shin, Y. Jiang, C. Jeong, H. A. Stone, and C. H. Choi, “Oil-Impregnated Nanoporous Oxide Layer for Corrosion Protection with Self-Healing,” Advanced Functional Materials, vol. 27, no. 15, article 1606040, 2017.
- X. Dai, N. Sun, S. O. Nielsen et al., “Hydrophilic directional slippery rough surfaces for water harvesting,” Science Advances, vol. 4, no. 3, article eaaq0919, 2018.
- K. Yin, S. Yang, X. Dong, D. Chu, J. A. Duan, and J. He, “Robust laser-structured asymmetrical PTFE mesh for underwater directional transportation and continuous collection of gas bubbles,” Applied Physics Letters, vol. 112, no. 24, article 243701, 2018.
- S. Yan, F. Ren, C. Li et al., “Unidirectional self-transport of air bubble via a Janus membrane in aqueous environment,” Applied Physics Letters, vol. 113, no. 26, article 261602, 2018.
- C. Pei, Y. Peng, Y. Zhang, D. Tian, K. Liu, and L. Jiang, “An integrated Janus mesh: underwater bubble antibuoyancy unidirectional penetration,” ACS Nano, vol. 12, no. 6, pp. 5489–5494, 2018.
- P. Xu, K. Ye, M. Du et al., “One-step synthesis of copper compounds on copper foil and their supercapacitive performance,” RSC Advances, vol. 5, no. 46, article 36656, 36664 pages, 2015.
- R. Ozbay, A. Kibar, and C. H. Choi, “Bubble adhesion to superhydrophilic surfaces,” in Advances in Contact Angle, Wettability and Adhesion, pp. 149–164, Wiley Online Library, 2015.
- A. Kibar, R. Ozbay, M. A. Sarshar, Y. T. Kang, and C. H. Choi, “Bubble movement on inclined hydrophobic surfaces,” Langmuir, vol. 33, no. 43, pp. 12016–12027, 2017.
- B. Jańczuk, “Adhesion of air bubbles to mineral surfaces in the presence of liquids,” Encyclopedia of Surface and Colloid Science, Taylor & Francis, pp. 97–112, 2nd edition, 2006.
- R. Tadmor, R. Das, S. Gulec et al., “Solid–liquid work of adhesion,” Langmuir, vol. 33, no. 15, pp. 3594–3600, 2017.
- J. Zhang and Y. Han, “Shape-gradient composite surfaces: water droplets move uphill,” Langmuir, vol. 23, no. 11, pp. 6136–6141, 2007.
Copyright © 2019 Jian Li and Zhiguang Guo. Exclusive Licensee Science and Technology Review Publishing House. Distributed under a Creative Commons Attribution License (CC BY 4.0).