Chenguang Fu, Satya N. Guin, Thomas Scaffidi, Yan Sun, Rana Saha, Sarah J. Watzman, Abhay K. Srivastava, Guowei Li, Walter Schnelle, Stuart S. P. Parkin, Claudia Felser, Johannes Gooth, "Largely Suppressed Magneto-Thermal Conductivity and Enhanced Magneto-Thermoelectric Properties in PtSn_{4}", *Research*, vol. 2020, Article ID 4643507, 8 pages, 2020. https://doi.org/10.34133/2020/4643507

# Largely Suppressed Magneto-Thermal Conductivity and Enhanced Magneto-Thermoelectric Properties in PtSn_{4}

#### Abstract

Highly conductive topological semimetals with exotic electronic structures offer fertile ground for the investigation of the electrical and thermal transport behavior of quasiparticles. Here, we find that the layer-structured Dirac semimetal PtSn_{4} exhibits a largely suppressed thermal conductivity under a magnetic field. At low temperatures, a dramatic decrease in the thermal conductivity of PtSn_{4} by more than two orders of magnitude is obtained at 9 T. Moreover, PtSn_{4} shows both strong longitudinal and transverse thermoelectric responses under a magnetic field. Large power factor and Nernst power factor of approximately 80–100 *μ*W·cm^{-1}·K^{-2} are obtained around 15 K in various magnetic fields. As a result, the thermoelectric figure of merit is strongly enhanced by more than 30 times, compared to that without a magnetic field. This work provides a paradigm for the decoupling of the electron and hole transport behavior of highly conductive topological semimetals and is helpful for developing topological semimetals for thermoelectric energy conversion.

#### 1. Introduction

In recent years, thermoelectric effects have attracted considerable attention in the fields of materials science and solid-state physics and chemistry. Practically, solid-state thermoelectric conversion offers a promising solution for energy harvesting and cooling [1]. Furthermore, investigations of thermoelectric phenomena are important for understanding the fundamental transport behavior of quasiparticles in solid materials [2]. The thermoelectric efficiency of a material is gauged by the figure of merit, , where , , , and are the thermopower, absolute temperature, electrical resistivity, and thermal conductivity, respectively. The term is known as the thermoelectric power factor. Although the expression is simple, obtaining a high is a challenging task because these transport parameters are interrelated. As a compromise, heavily doped semiconductors with moderate electrical conductivity and thermopower values have become the most widely investigated thermoelectric systems [3–5]. Metals or semimetals, owing to strong coupling of *S*, , and the electronic thermal conductivity , have attracted much less attention for thermoelectric studies. The key to developing metals or semimetals for thermoelectric application lies in the decoupling of the three electrical transport parameters.

In a two-carrier semimetal system, the thermopower is expressed as , where and indicate electrons and holes, respectively, and is the electrical conductivity. and generally have opposite signs and thus balance each other’s contribution to . Assuming the conduction and valence bands have symmetric structure and the Fermi level lies between them, the terms and will have similar values but opposite signs, so will be almost zero. Therefore, semimetals with symmetric conduction and valence bands have generally been viewed as poor thermoelectric materials. One way to overcome this disadvantage is to look for semimetals with a large asymmetry between the conduction and valence bands, where the large disparity in their electron and hole effective masses could ensure a sizable [6, 7]. Another recently proposed method of generating a large thermopower in topological Dirac/Weyl semimetals is to apply a sufficiently large magnetic field, under which the thermopower will grow linearly without saturation [8]. These proposals suggest feasible ways to tune the thermoelectric properties of topological semimetals.

When a conductive solid is placed under a longitudinal temperature gradient and a transverse magnetic field, two types of thermoelectric responses occur, i.e., the magneto-Seebeck effect in the longitudinal direction and the Nernst effect in the other transverse direction [9]. Both longitudinal and transverse thermoelectric effects have recently received attention in the studies of topological semimetals, specifically, studies of giant magnetic-field enhancement of the thermoelectric properties [10, 11] or exploration of the Berry curvature-related anomalous thermoelectric transport phenomena [12–18]. For instance, in the Dirac semimetal Cd_{3}As_{2} [19], which has ultrahigh carrier mobility [20], anomalous magneto-Seebeck and Nernst effects were recently observed [12, 14], and the relationship between these anomalous transport properties with Berry curvature was discussed. Moreover, the magnetic-field-induced giant enhancement in both longitudinal and transverse values were found in Cd_{3}As_{2} single crystals near room temperature [11, 21, 22]. NbP, one of the first type-I Weyl semimetals to be discovered [23–25], has recently attracted attention as a material platform for exploring the Weyl physics-related thermoelectric transport properties. Large magneto-thermopower and Nernst thermopower were observed in both single crystals and polycrystalline samples [10, 16, 26]. These findings demonstrate that topological semimetals provide fertile ground for exploring magnetic-field-mediated thermoelectric properties. Moreover, recent high-throughput searches have identified thousands of topological semimetals in the Inorganic Crystal Structure Database [27–29]. Among them, those with complex crystal structure or heavy elements would display high potential for magneto-thermoelectric conversion, as they could have an intrinsically low phonon thermal conductivity.

In this work, we study the electrical and thermal transport properties of the Dirac semimetal PtSn_{4} under a magnetic field. The Dirac nodal arc structure and high magnetoresistance (MR) in PtSn_{4} suggest that the electrical properties will respond strongly to a magnetic field [30, 31]; furthermore, the layered structure with planes stacked vertically along the axis (Figure 1(a)) and low Debye temperature of 210 K [31] suggest a low phonon thermal conductivity, which however has not been reported. In our experiments, we used PtSn_{4} single crystals grown from a Sn-rich binary melt [31]. The growth process and chemical and structural characterizations are described in the Methods section. The electrical resistivity , thermopower , Nernst thermopower , Hall resistivity , and thermal conductivity were measured at various magnetic fields, , up to 9 T. The details of the measurement procedure are also presented in the Methods section. All the transport experiments were conducted within the plane of the crystals, and the magnetic field is applied along the axis. The transport properties exhibited a dramatic response to the magnetic field below 30 K. When the magnetic field was applied, a large power factor of 80–100 *μ*W·cm^{-1}·K^{-2} and a very large suppression of the thermal conductivity appeared, which together contribute to an obvious increase in the peak at 15 K. Moreover, PtSn_{4} also exhibits a strong Nernst signal and a large Nernst power factor of 90 *μ*W·cm^{-1}·K^{-2} at 9 T and 10 K. These findings on PtSn_{4} provide a good paradigm for tuning highly conductive topological semimetals for simultaneous longitudinal and transverse thermoelectric energy conversion.

#### 2. Results and Discussion

In the first set of transport experiments at zero magnetic field, we confirm that the PtSn_{4} crystals exhibit the previously observed low electrical resistivity . In Figure 1(b), the measured is shown as a function of . In agreement with the literature [31], at zero field increases linearly with between 25 and 300 K, as expected for such semimetals, in which electron-phonon scattering is thought to dominate. Below 8 K, the resistivity starts to saturate, with a residual resistivity of 45 n*Ω*·cm at 2 K. Furthermore, a high residual resistance ratio of is observed, which, together with the nonsaturating MR up to 9 T, indicates a long carrier mean free path.

The absolute thermopower of PtSn_{4} at 0 T is much lower than that of typical thermoelectric semiconductors. is positive at high and exhibits a transition upon cooling (Figure 1(c)), indicating that PtSn_{4} is a two-carrier semimetal system. When the magnetic field is applied, depends strongly on at approximately 14 K, in agreement with the literature [31]. As a result, a moderate thermopower *μ*V·K^{-1} at 9 T is obtained. Even though the magnetic field also induces strong MR, large peak power factors of 80–100 *μ*W·cm^{-1}·K^{-2}, calculated by , are obtained under various magnetic fields (Figure 1(d)). Recalling that good thermoelectric materials generally have relatively low power factor, for example, Bi_{2}Te_{3} (30–50 *μ*W·cm^{-1}·K^{-2}) [32], PbTe (≈20 *μ*W·cm^{-1}·K^{-2}) [33, 34], SnSe (≈10 *μ*W·cm^{-1}·K^{-2}) [35], CoSb_{3} (30–50 *μ*W·cm^{-1}·K^{-2}) [36], and half-Heusler compounds (30–50 *μ*W·cm^{-1}·K^{-2}) [37], this large observed in PtSn_{4} under a magnetic field indicates its potential for thermoelectric conversion.

A large enhancement in is not the only required thermoelectric property; besides, the thermal conductivity should also be suppressed. We further measured the thermal conductivity of our samples as a function of temperature under various magnetic fields (Figure 1(e)). The experiments were performed with open electrical contact to prevent electric current flow. indicates a metallic dependence, which is consistent with the and measurements. Upon warming from 2 K, increases linearly with owing to the dominant impurity scattering. Near 8 K, reaches a maximum and then starts to decrease. Remarkably, exhibits a rapid decay with increasing . A decrease in by more than 2 orders of magnitude is observed at 9 T and 2 K. This huge suppression of is a result of the giant MR, which indicates that charge carriers, rather than phonons, dominate the thermal transport in PtSn_{4}. Owning to the magnetic-field-induced giant reduction in and enhancement of , PtSn_{4} exhibits a peak of 0.009 at 9 T and 15 K (Figure 1(f)), which is more than 30 times higher than the *zT* at zero field. Note that this peak in is obtained at a very low temperature of 15 K. The value, a more intrinsic material parameter reflecting the thermoelectric potential, is K^{-1} for PtSn_{4} at 9 T and 15 K, which is close to that of good thermoelectric materials, for example, Bi_{2}Te_{3} ( K^{-1}) [32], PbTe ( K^{-1}) [33, 34], CoSb_{3} ( K^{-1}) [36], and half-Heusler compounds ( K^{-1}) [37]. More importantly, this very large increase in the peak *zT* of PtSn_{4} results from the simultaneous improvement of and suppression of with increasing , which provides a good paradigm for the decoupling of the electrical and thermal transport properties.

To understand the magnetic-field-induced changes in the electrical transport properties, we further investigated the Hall resistivity as a function of at various . Upon cooling from 300 K, has a positive slope as a function of , indicating that holes dominate the transport. Below 50 K, the slope of reverses its sign at high fields. Because changes sign at low temperatures, especially around 25 K, it is tempting to associate this phenomenon with the transport contributions of both electrons and holes, which is also reflected by its thermopower at similar temperatures with almost 0 *μ*V·K^{-1}. Moreover, the Fermi surface of PtSn_{4} was calculated using density functional theory (Figure S1) and also indicates that PtSn_{4} is a two-carrier system with multiple electron and hole pockets.

For a more quantitative analysis of the carrier densities and mobilities, we calculated the Hall conductivity, (Figure 2(b)) using a two-carrier model:

This model enables us to obtain the temperature-dependent average carrier densities, , and the carrier mobilities , for the electron and hole pockets, respectively. The best fits to our data indeed reveal that our PtSn_{4} samples exhibit parallel transport of both electrons and holes across the full temperature range investigated (Figure 2(c)), with a hole excess above 50 K and an electron excess below. The electron and hole mobilities are very high (Figure 2(c), inset) and are comparable to those of the other topological semimetals [20, 25], in which the high mobility are responsible for the giant MR observed at low (Figure 1(b)).

After determining the carrier densities, we further investigated the thermopower as a function of around the temperatures at which peaks. As shown in Figure 2(d), a dramatic enhancement of occurs with increasing . The absolute magneto-thermopower, , becomes significant at higher magnetic fields ( T), exhibiting an approximately linear relationship with . The linear relationship at high magnetic fields can be understood in terms of the increase in the electron-phonon scattering rate with [38], yielding |MS| ≈ *ћ**ω*_{c}/*k*_{B}*T* for *ћω*_{c} > *k*_{B}*T*, where *ћ* and are the reduced Planck and Boltzmann constants, respectively. In addition, denotes the cyclotron frequency, where is the elementary charge. For an average effective mass, , a linear relation between |MS| and is expected above 3 T, in agreement with the experiments.

Considering the large carrier mobilities below 30 K and the strong response of the longitudinal thermopower to a magnetic field, it is tempting to check for the transverse thermoelectric response, i.e., the Nernst effect. The Nernst thermopower of PtSn_{4} at various temperatures was further measured by a standard one-heater, two-thermometer configuration. As shown in Figure 2(e), displays a normal Nernst signal, namely, an approximately linear increase upon magnetic-field application, and no saturation is found at magnetic fields of up to 9 T. At 9 T and 10.3 K, reaches a moderate value of 45 *μ*V·K^{-1}. Furthermore, because the electrical resistivity in the plane is approximately isotropic [39], the Nernst power factor can be estimated as (Figure 2(f)). Like the conventional power factor (Figure 1(d)), the Nernst power factor also peaks at approximately 15 K. A maximum value of approximately 90 *μ*W·cm^{-1}·K^{-2} is obtained at various magnetic fields, which is approximately 3 times larger than the value obtained in polycrystalline bulk NbP [10].

The thermal conductivity as a function of is shown in Figure 3(a). At 2 K, as the magnetic field increases, decreases by more than 2 orders of magnitude. The phonon thermal conductivity of a metallic system typically does not change significantly under a magnetic field. The very large decrease in is thus a result of the large MR (Figure 1(b)), which then makes it possible to separate the phonon and electron components of the thermal conductivity. An empirical expression, [40, 41], was employed to extract the phonon thermal conductivity, , and electron thermal conductivity, , at 0 T, where and are related to the thermal mobility and scattering mechanism, respectively. The obtained fitting parameters are shown in Table S1. Because this method is generally effective for large *μB*, only the data below 30 K were fitted. The fitted lines match the experimental data well, as shown in Figure 3(a), indicating the feasibility of this method. The extracted decreases continuously with increasing , as shown in Figure 3(b). At T, is significantly larger than , demonstrating that PtSn_{4} is indeed a metallic system in which charge carriers dominate the electrical and thermal transport properties. The Lorenz number is further calculated according to the Wiedemann–Franz (WF) law [1], as shown in Figure 3(c). At T, this is a downward violation of the WF law, whereas an upward violation is found when the magnetic field is applied. Violations of the WF law typically indicate inelastic electron-phonon scattering or hydrodynamic transport, as recently found in the Weyl semimetal WP_{2} [42, 43]. Moreover, in a very recent work on another Weyl semimetal system, TaP, Han et al. also observed an upward violation of the WF law [40]. The reason is still not clear, but it seems that violation of the WF law under a magnetic field is common in topological semimetals.

#### 3. Conclusions

In summary, measurements of the electrical and thermal transport properties established PtSn_{4} as a distinctive platform by exhibiting strong regulation of the two-carrier transport behavior under both a thermal gradient and a magnetic field. PtSn_{4} is a highly conductive topological semimetal with low electrical resistivity at liquid helium temperatures, which is comparable to that of many well-established metals or topological semimetals [44]. Hall effect measurement of PtSn_{4} revealed a two-carrier behavior with both high electron and high hole mobilities. At zero magnetic field, the thermopower is close to zero, and the thermal conductivity is orders of magnitude higher than that of good thermoelectric semiconductors. These features indicate that PtSn_{4} has a poor thermoelectric performance.

However, all these transport properties change significantly when a magnetic field is applied. Large Seebeck and Nernst power factors and a huge suppression of the thermal conductivity are simultaneously realized under various magnetic fields, providing a good example for decoupling the electrical and thermal transport properties of semimetals. These dramatic changes in the transport properties are the result of the regulation of the transport behavior of the two types of carriers under a magnetic field. At zero magnetic field, the thermal gradient drives the accumulation of both electrons and holes on the cold side, which balance each other’s contributions to the Seebeck thermopower. When a magnetic field is applied, the electrons and holes exhibit different transport behaviors, which makes it possible to realize strong thermoelectric responses in both the longitudinal and transverse directions. These results on PtSn_{4} provide a paradigm for tuning highly conductive semimetals for both longitudinal and transverse thermoelectric conversion by applying a magnetic field. Interestingly, some recent work had paid attention to the relationship between thermoelectric performance and internal magnetic interactions, for example, superparamagnetic behavior [45], paramagnon drag [46], and spin fluctuation [47]. These works together with our current study on PtSn_{4} demonstrate that introducing magnetic interaction as an additional influence on the transport properties, either by applying an external magnetic field or by introducing an internal magnetic moment, could open a new direction in thermoelectric research.

#### 4. Experimental Methods

Single crystals of PtSn_{4} were grown from a Sn-rich binary melt as described in the literature [31]. The high-purity starting elements, Pt (shot, 99.99%) and Sn (shot, 99.999%), were mixed with an initial stoichiometry of Pt_{4}Sn_{96}; the mixture was placed in an alumina crucible, which was sealed in a quartz tube under partial Ar pressure. The quartz tube was heated to 600°C over a period of 5 h and held at that temperature for 20 h. Next, it was slowly cooled to 350°C over a period of 60 h. The excess Sn flux was removed using a centrifuge at 400°C. After centrifugation, the remaining flux on the surface was removed by mechanical polishing.

Powder X-ray diffraction measurement of PtSn_{4} was performed using Cu K*α* radiation at room temperature to identify the phase purity and crystal structure. An image-plate Huber G670 Guinier camera was used in a diffraction range of in steps of 0.005°. Scanning electron microscopy (SEM) with energy-dispersive X-ray spectrometry (EDXS) was used for elemental analysis. Single-crystal X-ray diffraction measurements were performed using a Bruker D8 Venture diffractometer with Mo K*α* radiation and the SHELX97 software was used for structure refinement [48]. More information about the crystallographic and refinement parameters can be found in our previous work [49], where the studied PtSn_{4} single crystal is from the same batch with the current work. The crystal structure is described by the centrosymmetric space group *Ccca*, in agreement with the literature [50]. Figure 1(a) shows the layered crystal structure of PtSn_{4}, which consists of PtSn_{4} slabs constructed from eight-fold Sn-coordinated Pt atoms. The layered structure is visible in the SEM results, as shown in Figure S2. The layered nature of PtSn_{4} allows for slight disorder in the ac plane, i.e., a small misalignment between consecutive PtSn_{4} layers.

The powder X-ray diffraction pattern of PtSn_{4} is shown in Figure S3. The diffraction peaks can be well indexed to orthorhombic structure, in good agreement with the single-crystal X-ray diffraction results [49]. No other obvious phases are observed. The actual composition of the PtSn_{4} single crystal is determined by EDXS at seven randomly selected positions; the result agrees with the nominal composition within the instrument error, as shown in Table S2. High-resolution transmission electron microscopy (HRTEM) (Figure S4) of a *μ*m lamella showed the good crystallinity of the PtSn_{4} sample (Figure S5).

The temperature-dependent thermal conductivity and thermopower under a magnetic field were jointly measured adiabatically by the one-heater, two-thermometer configuration using the thermal transport option of the PPMS (Quantum Design), in which the sample was placed so that the magnetic field was perpendicular to the heat flow. The thermometers were calibrated under the magnetic field using the PPMS MR calibration wizard before the thermal transport measurements. To ensure uniform heat flow through the bar-shaped sample, two gold-plated copper leads were attached to both ends of the sample using silver epoxy and then connected to the heater and sink, respectively. Two other copper leads were wrapped around and glued to the sample with silver epoxy for detecting and . The applied temperature gradients were approximately 1%–3% of the base temperature. We then investigated the possible effect of the thermal contact resistances and demonstrated the need for careful contact preparation. After careful contact preparation, as described above, we investigated samples with lengths ranging from 4.5 to 7 mm, but similar cross-sections and contact areas. We obtained consistent results for all the samples at any magnetic field or temperature investigated, and therefore did not observe any indication of diminished thermal conductivity owing to contact. The Nernst thermopower was also measured adiabatically in the one-heater, two-thermometer configuration using the PPMS. The Nernst signal was estimated as, , where is the distance between the two temperature leads, *L _{y}* is the distance between the two voltage wires, is the transverse electric voltage, and is the measured temperature difference. The measured raw Nernst thermopower data were antisymmetrized to correct for contact misalignment.

Both the longitudinal and Hall resistivities were measured by a standard four-probe method using the AC transport option in the PPMS system with an applied AC current of 16 mA. Point contacts for Hall voltage probes were obtained by spot-welding 25 *μ*m platinum wires. For the current and longitudinal voltage probes, linear contacts were made using silver paint and platinum wires. To correct for contact misalignment, the measured Hall resistivity was field antisymmetrized. For all the transport measurements, the magnetic field was applied along the axis, which was perpendicular to the plane.

#### Conflicts of Interest

The authors declare no competing financial interest.

#### Acknowledgments

We acknowledge Jonah Waissman, Sean Hartnoll, and Subir Sachdev for valuable discussions, Machteld E. Kamminga for performing the single-crystal XRD studies, and Peter Werner for the help with TEM. This work was financially supported by the ERC advanced grant No. (742068) “TOP-MAT”. Ch.F. and S.N.G. acknowledge financial support from the Alexander von Humboldt Foundation. T.S. acknowledges support from the Emergent Phenomena in Quantum Systems initiative of the Gordon and Betty Moore Foundation. A.K.S. was funded by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation)—project number 314790414. M.E.K. was supported by The Netherlands Organization for Science NWO (graduate program 2013, No. 022.005.006).

#### Supplementary Materials

Fermi surface, SEM images, TEM images, XRD pattern, and EDX results.* (Supplementary Materials)*

#### References

- H. J. Goldsmid,
*Introduction of Thermoelectricity*, Springer, Heidelberg, 2010. - K. Behnia,
*Fundamentals of Thermoelectricity*, Oxford University Press, Oxford, 2015. - T. Zhu, Y. Liu, C. Fu, J. P. Heremans, J. G. Snyder, and X. Zhao, “Compromise and synergy in high-efficiency thermoelectric materials,”
*Advanced Materials*, vol. 29, no. 14, article 1605884, 2017. View at: Publisher Site | Google Scholar - T. Mori, “Novel principles and nanostructuring methods for enhanced thermoelectrics,”
*Small*, vol. 13, no. 45, article 1702013, 2017. View at: Publisher Site | Google Scholar - J. Mao, Z. Liu, J. Zhou et al., “Advances in thermoelectrics,”
*Advances in Physics*, vol. 67, no. 2, pp. 69–147, 2018. View at: Publisher Site | Google Scholar - M. Markov, X. Hu, H. C. Liu et al., “Semi-metals as potential thermoelectric materials,”
*Scientific Reports*, vol. 8, no. 1, p. 9876, 2018. View at: Publisher Site | Google Scholar - J. Mao, H. Zhu, Z. Ding et al., “High thermoelectric cooling performance of n-type Mg
_{3}Bi_{2}-based materials,”*Science*, vol. 365, no. 6452, pp. 495–498, 2019. View at: Publisher Site | Google Scholar - B. Skinner and L. Fu, “Large, nonsaturating thermopower in a quantizing magnetic field,”
*Science Advances*, vol. 4, no. 5, article eaat2621, 2018. View at: Publisher Site | Google Scholar - K. Behnia and H. Aubin, “Nernst effect in metals and superconductors: a review of concepts and experiments,”
*Reports on Progress in Physics*, vol. 79, no. 4, article 046502, 2016. View at: Google Scholar - C. Fu, S. N. Guin, S. J. Watzman et al., “Large Nernst power factor over a broad temperature range in polycrystalline Weyl semimetal NbP,”
*Energy & Environmental Science*, vol. 11, no. 10, pp. 2813–2820, 2018. View at: Publisher Site | Google Scholar - H. Wang, X. Luo, W. Chen et al., “Magnetic-field enhanced high-thermoelectric performance in topological Dirac semimetal Cd
_{3}As_{2}crystal,”*Science Bulletin*, vol. 63, no. 7, pp. 411–418, 2018. View at: Publisher Site | Google Scholar - Z. Jia, C. Li, X. Li et al., “Thermoelectric signature of the chiral anomaly in Cd
_{3}As_{2},”*Nature Communications*, vol. 7, no. 1, article 13013, 2016. View at: Publisher Site | Google Scholar - X. Li, L. Xu, L. Ding et al., “Anomalous Nernst and Righi-Leduc effects inMn3Sn: Berry curvature and entropy flow,”
*Physical Review Letters*, vol. 119, no. 5, article 056601, 2017. View at: Publisher Site | Google Scholar - T. Liang, J. Lin, Q. Gibson et al., “Anomalous Nernst Effect in the Dirac Semimetal Cd
_{3}As_{2},”*Physical Review Letters*, vol. 118, no. 13, article 136601, 2017. View at: Publisher Site | Google Scholar - A. Sakai, Y. P. Mizuta, A. A. Nugroho et al., “Giant anomalous Nernst effect and quantum-critical scaling in a ferromagnetic semimetal,”
*Nature Physics*, vol. 14, no. 11, pp. 1119–1124, 2018. View at: Publisher Site | Google Scholar - S. J. Watzman, T. M. McCormick, C. Shekhar et al., “Dirac dispersion generates unusually large Nernst effect in Weyl semimetals,”
*Physical Review B*, vol. 97, no. 16, article 161404, 2018. View at: Publisher Site | Google Scholar - S. N. Guin, K. Manna, J. Noky et al., “Anomalous Nernst effect beyond the magnetization scaling relation in the ferromagnetic Heusler compound Co
_{2}MnGa,”*NPG Asia Materials*, vol. 11, no. 1, article 16, 2019. View at: Publisher Site | Google Scholar - S. N. Guin, P. Vir, Y. Zhang et al., “Zero-field Nernst effect in a ferromagnetic Kagome-Lattice Weyl-semimetal Co
_{3}Sn_{2}S_{2},”*Advanced Materials*, vol. 31, no. 25, article 1806622, 2019. View at: Publisher Site | Google Scholar - Z. Wang, H. Weng, Q. Wu, X. Dai, and Z. Fang, “Three-dimensional Dirac semimetal and quantum transport in Cd
_{3}As_{2},”*Physical Review B*, vol. 88, no. 12, article 125427, 2013. View at: Publisher Site | Google Scholar - T. Liang, Q. Gibson, M. N. Ali, M. Liu, R. J. Cava, and N. P. Ong, “Ultrahigh mobility and giant magnetoresistance in the Dirac semimetal Cd
_{3}As_{2},”*Nature Materials*, vol. 14, no. 3, pp. 280–284, 2014. View at: Publisher Site | Google Scholar - H. Wang, X. Luo, K. Peng et al., “Magnetic field-enhanced thermoelectric performance in Dirac semimetal Cd
_{3}As_{2}crystals with different carrier concentrations,”*Advanced Functional Materials*, vol. 29, no. 37, article 1902437, 2019. View at: Publisher Site | Google Scholar - J. Xiang, S. L. Hu, M. Lyu et al., “Large transverse thermoelectric figure of merit in a topological Dirac semimetal,”
*Science China Physics, Mechanics & Astronomy*, vol. 63, no. 3, article 237011, 2020. View at: Publisher Site | Google Scholar - H. Weng, C. Fang, Z. Fang, B. A. Bernevig, and X. Dai, “Weyl semimetal phase in noncentrosymmetric transition-metal monophosphides,”
*Physical Review X*, vol. 5, no. 1, article 011029, 2015. View at: Publisher Site | Google Scholar - S.-Y. Xu, I. Belopolski, N. Alidoust et al., “Discovery of a Weyl fermion semimetal and topological Fermi arcs,”
*Science*, vol. 349, no. 6248, pp. 613–617, 2015. View at: Publisher Site | Google Scholar - C. Shekhar, A. K. Nayak, Y. Sun et al., “Extremely large magnetoresistance and ultrahigh mobility in the topological Weyl semimetal candidate NbP,”
*Nature Physics*, vol. 11, no. 8, pp. 645–649, 2015. View at: Publisher Site | Google Scholar - U. Stockert, R. D. Dos Reis, M. O. Ajeesh et al., “Thermopower and thermal conductivity in the Weyl semimetal NbP,”
*Journal of Physics: Condensed Matter*, vol. 29, no. 32, article 325701, 2017. View at: Publisher Site | Google Scholar - M. G. Vergniory, L. Elcoro, C. Felser, N. Regnault, B. A. Bernevig, and Z. Wang, “A complete catalogue of high-quality topological materials,”
*Nature*, vol. 566, no. 7745, pp. 480–485, 2019. View at: Publisher Site | Google Scholar - F. Tang, H. C. Po, A. Vishwanath, and X. Wan, “Comprehensive search for topological materials using symmetry indicators,”
*Nature*, vol. 566, no. 7745, pp. 486–489, 2019. View at: Publisher Site | Google Scholar - T. Zhang, Y. Jiang, Z. Song et al., “Catalogue of topological electronic materials,”
*Nature*, vol. 566, no. 7745, pp. 475–479, 2019. View at: Publisher Site | Google Scholar - Y. Wu, L. L. Wang, E. Mun et al., “Dirac node arcs in PtSn
_{4},”*Nature Physics*, vol. 12, no. 7, pp. 667–671, 2016. View at: Publisher Site | Google Scholar - E. Mun, H. Ko, G. J. Miller, G. D. Samolyuk, S. L. Bud'ko, and P. C. Canfield, “Magnetic field effects on transport properties of PtSn
_{4},”*Physical Review B*, vol. 85, no. 3, article 035135, 2012. View at: Publisher Site | Google Scholar - B. Poudel, Q. Hao, Y. Ma et al., “High-thermoelectric performance of nanostructured bismuth antimony telluride bulk alloys,”
*Science*, vol. 320, no. 5876, pp. 634–638, 2008. View at: Publisher Site | Google Scholar - Y. Pei, X. Shi, A. LaLonde, H. Wang, L. Chen, and G. J. Snyder, “Convergence of electronic bands for high performance bulk thermoelectrics,”
*Nature*, vol. 473, no. 7345, pp. 66–69, 2011. View at: Publisher Site | Google Scholar - K. Biswas, J. He, I. D. Blum et al., “High-performance bulk thermoelectrics with all-scale hierarchical architectures,”
*Nature*, vol. 489, no. 7416, pp. 414–418, 2012. View at: Publisher Site | Google Scholar - P.-P. Shang, J. Dong, J. Pei et al., “Highly textured N-type SnSe polycrystals with enhanced thermoelectric performance,”
*Research*, vol. 2019, article 9253132, 10 pages, 2019. View at: Publisher Site | Google Scholar - X. Shi, J. Yang, J. R. Salvador et al., “Multiple-filled Skutterudites: high thermoelectric figure of merit through separately optimizing electrical and thermal transports,”
*Journal of the American Chemical Society*, vol. 133, no. 20, pp. 7837–7846, 2011. View at: Publisher Site | Google Scholar - C. Fu, T. Zhu, Y. Liu, H. Xie, and X. Zhao, “Band engineering of high performance p-type FeNbSb based half-Heusler thermoelectric materials for figure of merit
*zT*> 1,”*Energy & Environmental Science*, vol. 8, no. 1, pp. 216–220, 2015. View at: Publisher Site | Google Scholar - T. Ohta, “Phonon-drag Seebeck effect in a strong magnetic field (1) longitudinal case,”
*Journal of the Physical Society of Japan*, vol. 18, no. 8, pp. 1166–1173, 1963. View at: Publisher Site | Google Scholar - M. Inamdar, M. Kriegisch, L. Shafeek et al., “Quantum oscillations in ultra pure PtSn
_{4},”*Solid State Phenomena*, vol. 194, pp. 88–91, 2012. View at: Publisher Site | Google Scholar - F. Han, N. Andrejevic, T. Nguyen et al., “Discovery of giant, non-saturating thermopower in topological semimetal at quantum limit,” 2019, http://arxiv.org/abs/1904.03179. View at: Google Scholar
- R. Ocaña and P. Esquinazi, “Thermal conductivity tensor in YBa
_{2}Cu_{3}O_{7−x}: effects of a planar magnetic field,”*Physical Review B*, vol. 66, no. 6, 2002. View at: Publisher Site | Google Scholar - J. Gooth, F. Menges, N. Kumar et al., “Thermal and electrical signatures of a hydrodynamic electron fluid in tungsten diphosphide,”
*Nature Communications*, vol. 9, no. 1, article 4093, 2018. View at: Publisher Site | Google Scholar - A. Jaoui, B. Fauqué, C. W. Rischau et al., “Departure from the Wiedemann–Franz law in WP
_{2}driven by mismatch in*T*-square resistivity prefactors,”*npj Quantum Materials*, vol. 3, no. 1, article 64, 2018. View at: Publisher Site | Google Scholar - J. Hu, S. Y. Xu, N. Ni, and Z. Mao, “Transport of topological semimetals,”
*Annual Review of Materials Research*, vol. 49, no. 1, pp. 207–252, 2019. View at: Publisher Site | Google Scholar - W. Zhao, Z. Liu, Z. Sun et al., “Superparamagnetic enhancement of thermoelectric performance,”
*Nature*, vol. 549, no. 7671, pp. 247–251, 2017. View at: Publisher Site | Google Scholar - Y. Zheng, T. Lu, M. M. H. Polash et al., “Paramagnon drag in high thermoelectric figure of merit Li-doped MnTe,”
*Science Advances*, vol. 5, no. 9, article eaat9461, 2019. View at: Publisher Site | Google Scholar - N. Tsujii, A. Nishide, J. Hayakawa, and T. Mori, “Observation of enhanced thermopower due to spin fluctuation in weak itinerant ferromagnet,”
*Science Advances*, vol. 5, no. 2, article eaat5935, 2019. View at: Publisher Site | Google Scholar - G. M. Sheldrick,
*Program for Crystal Structure Refinement*, University of Göttingen, Göttingen, 1997. - G. Li, C. Fu, W. Shi et al., “Dirac nodal arc semimetal PtSn
_{4}: an ideal platform for understanding surface properties and catalysis for hydrogen evolution,”*Angewandte Chemie*, vol. 131, no. 37, pp. 13241–13246, 2019. View at: Publisher Site | Google Scholar - B. Künnen, D. Niepmann, and W. Jeitschko, “Structure refinements and some properties of the transition metal stannides Os
_{3}Sn_{7}, Ir_{5}Sn_{7}, Ni_{0.402(4)}Pd_{0.598}Sn_{4},*α*-PdSn_{2}and PtSn_{4},”*Journal of Alloys and Compounds*, vol. 309, no. 1-2, pp. 1–9, 2000. View at: Publisher Site | Google Scholar

#### Copyright

Copyright © 2020 Chenguang Fu et al. Exclusive Licensee Science and Technology Review Publishing House. Distributed under a Creative Commons Attribution License (CC BY 4.0).